题名: Studies on the corrosion behavior of Fe-20Cr alloy in NaCl solution spray at 600 degrees C
作者: Cao, M;  Liu, L;  Yu, ZF;  Fan, L;  Ying, L;  Wang, FH
发表日期: 2018-4-1
摘要: The corrosion behavior of Fe-20Cr in NaCl solution spray at 600 degrees C, compared with that under solid NaCl deposit in water vapor, has been studied by mass-gain measurements, scanning electron microscopy, X-ray diffraction, X-ray photoelectron spectroscopy, secondary ion mass spectrometry and transmission electron microscopy methods The results demonstrated that Fe-20Cr undergoes serious corrosion in NaCl solution spray. Significantly different corrosion products with outer Fe2O3 and inner FeCr2O4 layers were formed. Meanwhile, a small amount of Cl was found In the corrosion scale, which was thought to have an important effect on corrosion. The corrosion behavior of Fe-20Cr in NaCl solution spray at 600 degrees C has been discussed in detail.
刊名: CORROSION SCIENCE
Appears in Collections:中国科学院金属研究所_期刊论文

Files in This Item:

There are no files associated with this item.




Recommended Citation:
Cao, M,Liu, L,Yu, ZF,et al. Studies On The Corrosion Behavior Of Fe-20cr Alloy In Nacl Solution Spray At 600 Degrees C[J]. Corrosion Science,2018,133:165-177.

SCI Citaion Data:
Service
 Recommend this item
 Sava as my favorate item
 Show this item's statistics
 Export Endnote File
Google Scholar
 Similar articles in Google Scholar
 [Cao, M]'s Articles
 [Liu, L]'s Articles
 [Yu, ZF]'s Articles
CSDL cross search
 Similar articles in CSDL Cross Search
 [Cao, M]‘s Articles
 [Liu, L]‘s Articles
 [Yu, ZF]‘s Articles
Scirus search
 Similar articles in Scirus
Related Copyright Policies
Null
Social Bookmarking
  Add to CiteULike  Add to Connotea  Add to Del.icio.us  Add to Digg  Add to Reddit 
所有评论 (0)
暂无评论
 
评注功能仅针对注册用户开放,请您登录
您对该条目有什么异议,请填写以下表单,管理员会尽快联系您。
内 容:
Email:  *
单位:
验证码:   刷新
您在IR的使用过程中有什么好的想法或者建议可以反馈给我们。
标 题:
 *
内 容:
Email:  *
验证码:   刷新

Items in IR are protected by copyright, with all rights reserved, unless otherwise indicated.

 

 

Valid XHTML 1.0!
Copyright © 2007-2018  中国科学院金属研究所  -Feedback
Powered by CSpace