| Fretting corrosion fatigue of Alloy 690 in high-temperature pure water | |
| Liao, JP; Wu, XQ; Tan, JB; Tang, LC; Qian, H; Xie, YC; Wu, XQ (reprint author), Chinese Acad Sci, Inst Met Res, CAS Key Lab Nucl Mat & Safety Assessment, Liaoning Key Lab Safety & Assessment Tech Nucl Ma, Shenyang 110016, Liaoning, Peoples R China. | |
| 2018-04-01 | |
| Source Publication | CORROSION SCIENCE
 |
| ISSN | 0010-938X |
| Volume | 133Pages:423-431 |
| Abstract | Fretting fatigue behavior of Alloy 690 in room-temperature (RT) air and high-temperature pure water was investigated under the condition of a normal load of 100 N. Fretting fatigue life in high-temperature water reduced by about 30% compared to that in RT air due to combined effects of high-temperature water and highly localized tangential stress. The main fatigue cracks were inclined to initiate in the crevice region along the contact edges in high-temperature water, but none was observed in RT air. Related mechanisms of fretting corrosion fatigue failure of Alloy 690 in high-temperature water are discussed.; Fretting fatigue behavior of Alloy 690 in room-temperature (RT) air and high-temperature pure water was investigated under the condition of a normal load of 100 N. Fretting fatigue life in high-temperature water reduced by about 30% compared to that in RT air due to combined effects of high-temperature water and highly localized tangential stress. The main fatigue cracks were inclined to initiate in the crevice region along the contact edges in high-temperature water, but none was observed in RT air. Related mechanisms of fretting corrosion fatigue failure of Alloy 690 in high-temperature water are discussed. |
| description.department | [liao, jiapeng ; wu, xinqiang ; tan, jibo] chinese acad sci, inst met res, cas key lab nucl mat & safety assessment, liaoning key lab safety & assessment tech nucl ma, shenyang 110016, liaoning, peoples r china ; [liao, jiapeng] univ sci & technol china, sch mat sci & engn, hefei 230026, anhui, peoples r china ; [tang, lichen ; qian, hao ; xie, yongcheng] shanghai nucl engn res & design inst, shanghai 200233, peoples r china |
| Keyword | Steam-generator Tubes Surface Oxide-films Crevice Corrosion Stress-corrosion Stainless-steel Wear Behavior Nickel-alloys 304-stainless-steel Environments Mechanism |
| Subject Area | Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering |
| Funding Organization | National Natural Science Foundation of China [51671201]; Chinese Academy of Sciences (Research on the Development of Nuclear Power Materials and Service Security Technology) [ZDRW-CN-2017-1]; Institute of Metal Research, Chinese Academy of Sciences [SCJJ-2013-ZD-02] |
| Indexed By | SCI |
| Language | 英语 |
| Document Type | 期刊论文 |
| Identifier | http://ir.imr.ac.cn/handle/321006/79388 |
| Collection | 中国科学院金属研究所 |
| Corresponding Author | Wu, XQ (reprint author), Chinese Acad Sci, Inst Met Res, CAS Key Lab Nucl Mat & Safety Assessment, Liaoning Key Lab Safety & Assessment Tech Nucl Ma, Shenyang 110016, Liaoning, Peoples R China. |
| Recommended Citation GB/T 7714 | Liao, JP,Wu, XQ,Tan, JB,et al. Fretting corrosion fatigue of Alloy 690 in high-temperature pure water[J]. CORROSION SCIENCE,2018,133:423-431. |
| APA | Liao, JP.,Wu, XQ.,Tan, JB.,Tang, LC.,Qian, H.,...&Wu, XQ .(2018).Fretting corrosion fatigue of Alloy 690 in high-temperature pure water.CORROSION SCIENCE,133,423-431. |
| MLA | Liao, JP,et al."Fretting corrosion fatigue of Alloy 690 in high-temperature pure water".CORROSION SCIENCE 133(2018):423-431. |
| Files in This Item: | There are no files associated with this item. | |||||
Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.
Edit Comment