Fretting corrosion fatigue of Alloy 690 in high-temperature pure water

IMR OpenIR

	Fretting corrosion fatigue of Alloy 690 in high-temperature pure water
	Liao, JP; Wu, XQ; Tan, JB; Tang, LC; Qian, H; Xie, YC; Wu, XQ (reprint author), Chinese Acad Sci, Inst Met Res, CAS Key Lab Nucl Mat & Safety Assessment, Liaoning Key Lab Safety & Assessment Tech Nucl Ma, Shenyang 110016, Liaoning, Peoples R China.
	2018-04-01
发表期刊	CORROSION SCIENCE
ISSN	0010-938X
卷号	133 页码:423-431
摘要	Fretting fatigue behavior of Alloy 690 in room-temperature (RT) air and high-temperature pure water was investigated under the condition of a normal load of 100 N. Fretting fatigue life in high-temperature water reduced by about 30% compared to that in RT air due to combined effects of high-temperature water and highly localized tangential stress. The main fatigue cracks were inclined to initiate in the crevice region along the contact edges in high-temperature water, but none was observed in RT air. Related mechanisms of fretting corrosion fatigue failure of Alloy 690 in high-temperature water are discussed.; Fretting fatigue behavior of Alloy 690 in room-temperature (RT) air and high-temperature pure water was investigated under the condition of a normal load of 100 N. Fretting fatigue life in high-temperature water reduced by about 30% compared to that in RT air due to combined effects of high-temperature water and highly localized tangential stress. The main fatigue cracks were inclined to initiate in the crevice region along the contact edges in high-temperature water, but none was observed in RT air. Related mechanisms of fretting corrosion fatigue failure of Alloy 690 in high-temperature water are discussed.
部门归属	[liao, jiapeng ; wu, xinqiang ; tan, jibo] chinese acad sci, inst met res, cas key lab nucl mat & safety assessment, liaoning key lab safety & assessment tech nucl ma, shenyang 110016, liaoning, peoples r china ; [liao, jiapeng] univ sci & technol china, sch mat sci & engn, hefei 230026, anhui, peoples r china ; [tang, lichen ; qian, hao ; xie, yongcheng] shanghai nucl engn res & design inst, shanghai 200233, peoples r china
关键词	Steam-generator Tubes Surface Oxide-films Crevice Corrosion Stress-corrosion Stainless-steel Wear Behavior Nickel-alloys 304-stainless-steel Environments Mechanism
学科领域	Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering
资助者	National Natural Science Foundation of China [51671201]; Chinese Academy of Sciences (Research on the Development of Nuclear Power Materials and Service Security Technology) [ZDRW-CN-2017-1]; Institute of Metal Research, Chinese Academy of Sciences [SCJJ-2013-ZD-02]
收录类别	SCI
语种	英语
WOS记录号	WOS:000429764100039
引用统计	被引频次：26[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/79388
专题	中国科学院金属研究所
通讯作者	Wu, XQ (reprint author), Chinese Acad Sci, Inst Met Res, CAS Key Lab Nucl Mat & Safety Assessment, Liaoning Key Lab Safety & Assessment Tech Nucl Ma, Shenyang 110016, Liaoning, Peoples R China.
推荐引用方式 GB/T 7714	Liao, JP,Wu, XQ,Tan, JB,et al. Fretting corrosion fatigue of Alloy 690 in high-temperature pure water[J]. CORROSION SCIENCE,2018,133:423-431.
APA	Liao, JP.,Wu, XQ.,Tan, JB.,Tang, LC.,Qian, H.,...&Wu, XQ .(2018).Fretting corrosion fatigue of Alloy 690 in high-temperature pure water.CORROSION SCIENCE,133,423-431.
MLA	Liao, JP,et al."Fretting corrosion fatigue of Alloy 690 in high-temperature pure water".CORROSION SCIENCE 133(2018):423-431.