Porous TiAl3 intermetallics with symmetrical graded pore-structure fabricated by leaching space holder and thermal explosion process

IMR OpenIR

	Porous TiAl3 intermetallics with symmetrical graded pore-structure fabricated by leaching space holder and thermal explosion process
	Jiao, XY; Ren, XR; Wang, XH; Wang, SG; Feng, PZ; Wang, JZ; Feng, PZ (reprint author), China Univ Min & Technol, Sch Mat Sci & Engn, Xuzhou 221116, Peoples R China.
	2018-04-01
发表期刊	INTERMETALLICS
ISSN	0966-9795
卷号	95 页码:144-149
摘要	High porosity of porous TiAl3 intermetallics were prepared from Ti-75Al at.% elemental powders by NaCl as temporary space holder, combining with multilayer stacking technology and thermal explosion reaction. Results showed that space holder particles in green compact were completely removed before sintering and only single TiAl3 phases were synthesized in sintered product. The porosity (>70%) can be easily obtained when adding 0, 30 or 50 vol.% NaCl in designed layers. SEM image indicated that the distribution of small pores ( <80 mu m) was uniform and embedded in pore walls of the skeleton without NaCl space holder. Large pores (300-500 mu m) began to appear when added the NaCl particles and the number of large pores improved with the increase of space holder content. The sintered discs with three or five sintered layers exhibited a symmetrical graded pore size distribution: large pores replicating from space holder and small pores generated during the sintering process. The graded pore-structure can be designed by adjusting the compact structure in each layer, allowing for a widespread applications in specific filtration units and liquid-gas separation.; High porosity of porous TiAl3 intermetallics were prepared from Ti-75Al at.% elemental powders by NaCl as temporary space holder, combining with multilayer stacking technology and thermal explosion reaction. Results showed that space holder particles in green compact were completely removed before sintering and only single TiAl3 phases were synthesized in sintered product. The porosity (>70%) can be easily obtained when adding 0, 30 or 50 vol.% NaCl in designed layers. SEM image indicated that the distribution of small pores ( <80 mu m) was uniform and embedded in pore walls of the skeleton without NaCl space holder. Large pores (300-500 mu m) began to appear when added the NaCl particles and the number of large pores improved with the increase of space holder content. The sintered discs with three or five sintered layers exhibited a symmetrical graded pore size distribution: large pores replicating from space holder and small pores generated during the sintering process. The graded pore-structure can be designed by adjusting the compact structure in each layer, allowing for a widespread applications in specific filtration units and liquid-gas separation.
部门归属	[jiao, xinyang ; ren, xuanru ; wang, xiaohong ; feng, peizhong] china univ min & technol, sch mat sci & engn, xuzhou 221116, peoples r china ; [jiao, xinyang] china univ min & technol, sch chem engn & technol, xuzhou 221116, peoples r china ; [wang, shaogang] chinese acad sci, shenyang natl lab mat sci, inst met res, shenyang 110016, liaoning, peoples r china ; [wang, jianzhong] northwest inst nonferrous met res, state key lab porous met mat, xian 710016, shaanxi, peoples r china
关键词	Ti-al Combustion Synthesis Heat-treatment Alloys Temperature Behavior Mode Foam
学科领域	Chemistry, Physical ; Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering
资助者	National Natural Science Foundation of China [51574241]; bilateral project of NSFC-STINT [51611130064]; Program for Innovation Research Team of China University of Mining and Technology [2015QN004]
收录类别	SCI
语种	英语
WOS记录号	WOS:000428975100019
引用统计	被引频次：21[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/79394
专题	中国科学院金属研究所
通讯作者	Feng, PZ (reprint author), China Univ Min & Technol, Sch Mat Sci & Engn, Xuzhou 221116, Peoples R China.
推荐引用方式 GB/T 7714	Jiao, XY,Ren, XR,Wang, XH,et al. Porous TiAl3 intermetallics with symmetrical graded pore-structure fabricated by leaching space holder and thermal explosion process[J]. INTERMETALLICS,2018,95:144-149.
APA	Jiao, XY.,Ren, XR.,Wang, XH.,Wang, SG.,Feng, PZ.,...&Feng, PZ .(2018).Porous TiAl3 intermetallics with symmetrical graded pore-structure fabricated by leaching space holder and thermal explosion process.INTERMETALLICS,95,144-149.
MLA	Jiao, XY,et al."Porous TiAl3 intermetallics with symmetrical graded pore-structure fabricated by leaching space holder and thermal explosion process".INTERMETALLICS 95(2018):144-149.