Roles of Mn in the High-Temperature Air Oxidation of 9Cr Ferritic-Martensitic Steel After Severe Plastic Deformation
Chen, SH; Rong, LJ; Rong, LJ (reprint author), Chinese Acad Sci, Inst Met Res, Key Lab Nucl Mat & Safety Assessment, 72 Wenhua Rd, Shenyang 110016, Liaoning, Peoples R China.
2018-04-01
发表期刊OXIDATION OF METALS
ISSN0030-770X
卷号89期号:43163页码:415-428
摘要Oxidation resistance of 9Cr ferritic-martensitic steel before and after cold-swaging process in air at 923 K was compared, and the oxide scales were characterized in detail by secondary ion mass spectrometry (SIMS). Both the cold-swaged sample and post-annealed samples showed considerably greater oxidation resistance than the initial as-tempered sample. Mn played a key role in scale formation of the cold-swaged sample and post-annealed sample; although the Mn content was only 0.5 wt% in the matrix, formation of Mn oxide (MnCr2O4 and Mn2O3) was favored. Roles of Mn in the oxidation behaviors of the cold-swaged sample and post-annealed sample were discussed.; Oxidation resistance of 9Cr ferritic-martensitic steel before and after cold-swaging process in air at 923 K was compared, and the oxide scales were characterized in detail by secondary ion mass spectrometry (SIMS). Both the cold-swaged sample and post-annealed samples showed considerably greater oxidation resistance than the initial as-tempered sample. Mn played a key role in scale formation of the cold-swaged sample and post-annealed sample; although the Mn content was only 0.5 wt% in the matrix, formation of Mn oxide (MnCr2O4 and Mn2O3) was favored. Roles of Mn in the oxidation behaviors of the cold-swaged sample and post-annealed sample were discussed.
部门归属[chen, shenghu ; rong, lijian] chinese acad sci, inst met res, key lab nucl mat & safety assessment, 72 wenhua rd, shenyang 110016, liaoning, peoples r china
关键词Mechanical Attrition Treatment Iron-base Alloys Carbon-dioxide Diffusion Behavior Resistance Corrosion Microstructure Chromium
学科领域Metallurgy & Metallurgical Engineering
资助者Major Research Plan of the National Natural Science Foundation of China [91226204]; Innovation Foundation of IMR [2015-PY10]
收录类别SCI
语种英语
文献类型期刊论文
条目标识符http://ir.imr.ac.cn/handle/321006/79409
专题中国科学院金属研究所
通讯作者Chen, SH; Rong, LJ (reprint author), Chinese Acad Sci, Inst Met Res, Key Lab Nucl Mat & Safety Assessment, 72 Wenhua Rd, Shenyang 110016, Liaoning, Peoples R China.
推荐引用方式
GB/T 7714
Chen, SH,Rong, LJ,Rong, LJ . Roles of Mn in the High-Temperature Air Oxidation of 9Cr Ferritic-Martensitic Steel After Severe Plastic Deformation[J]. OXIDATION OF METALS,2018,89(43163):415-428.
APA Chen, SH,Rong, LJ,&Rong, LJ .(2018).Roles of Mn in the High-Temperature Air Oxidation of 9Cr Ferritic-Martensitic Steel After Severe Plastic Deformation.OXIDATION OF METALS,89(43163),415-428.
MLA Chen, SH,et al."Roles of Mn in the High-Temperature Air Oxidation of 9Cr Ferritic-Martensitic Steel After Severe Plastic Deformation".OXIDATION OF METALS 89.43163(2018):415-428.
条目包含的文件
条目无相关文件。
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[Chen, SH]的文章
[Rong, LJ]的文章
[Rong, LJ (reprint author), Chinese Acad Sci, Inst Met Res, Key Lab Nucl Mat & Safety Assessment, 72 Wenhua Rd, Shenyang 110016, Liaoning, Peoples R China.]的文章
百度学术
百度学术中相似的文章
[Chen, SH]的文章
[Rong, LJ]的文章
[Rong, LJ (reprint author), Chinese Acad Sci, Inst Met Res, Key Lab Nucl Mat & Safety Assessment, 72 Wenhua Rd, Shenyang 110016, Liaoning, Peoples R China.]的文章
必应学术
必应学术中相似的文章
[Chen, SH]的文章
[Rong, LJ]的文章
[Rong, LJ (reprint author), Chinese Acad Sci, Inst Met Res, Key Lab Nucl Mat & Safety Assessment, 72 Wenhua Rd, Shenyang 110016, Liaoning, Peoples R China.]的文章
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。