| Anisotropy of high temperature creep properties of a Co-base single crystal superalloy | |
| Lu, YZ; Xie, G; Wang, D; Zhang, SH; Zheng, W; Shen, J; Lou, LH; Zhang, J; Zhang, J (reprint author), Chinese Acad Sci, Inst Met Res, Shenyang 110016, Liaoning, Peoples R China. | |
| 2018-03-21 | |
| Source Publication | MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
 |
| ISSN | 0921-5093 |
| Volume | 720Pages:69-74 |
| Abstract | The orientation dependence of creep properties of a Co-base single crystal superalloy at 982 degrees C/248 MPa was investigated. The orientations of specimens tested were near [001, 011] and [111]. The results showed the deformation of these specimens was all controlled by a/3 < 112 > slip and stacking faults. The specimens with orientation near [001] exhibited the best creep resistance. There were a few stacking faults with two orientations in the specimens with [001] orientation. Specimens with orientations near [111] and [011] showed shorter creep lives, and stacking faults with single orientation were observed.; The orientation dependence of creep properties of a Co-base single crystal superalloy at 982 degrees C/248 MPa was investigated. The orientations of specimens tested were near [001, 011] and [111]. The results showed the deformation of these specimens was all controlled by a/3 < 112 > slip and stacking faults. The specimens with orientation near [001] exhibited the best creep resistance. There were a few stacking faults with two orientations in the specimens with [001] orientation. Specimens with orientations near [111] and [011] showed shorter creep lives, and stacking faults with single orientation were observed. |
| description.department | [lu, yuzhang ; xie, guang ; wang, dong ; zhang, shaohua ; zheng, wei ; shen, jian ; lou, langhong ; zhang, jian] chinese acad sci, inst met res, shenyang 110016, liaoning, peoples r china |
| Keyword | Alloys Deformation Ta Ti |
| Subject Area | Nanoscience & Nanotechnology ; Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering |
| Funding Organization | National Key Research and Development Program of China [2017YFB0702904]; National Natural Science Foundation of China [51631008, 51771204, U1732131]; Scientific Research Equipment Development Project of Chinese Academy of Sciences [YZ201529] |
| Indexed By | SCI |
| Language | 英语 |
| Document Type | 期刊论文 |
| Identifier | http://ir.imr.ac.cn/handle/321006/79422 |
| Collection | 中国科学院金属研究所 |
| Corresponding Author | Zhang, J (reprint author), Chinese Acad Sci, Inst Met Res, Shenyang 110016, Liaoning, Peoples R China. |
| Recommended Citation GB/T 7714 | Lu, YZ,Xie, G,Wang, D,et al. Anisotropy of high temperature creep properties of a Co-base single crystal superalloy[J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,2018,720:69-74. |
| APA | Lu, YZ.,Xie, G.,Wang, D.,Zhang, SH.,Zheng, W.,...&Zhang, J .(2018).Anisotropy of high temperature creep properties of a Co-base single crystal superalloy.MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,720,69-74. |
| MLA | Lu, YZ,et al."Anisotropy of high temperature creep properties of a Co-base single crystal superalloy".MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING 720(2018):69-74. |
| Files in This Item: | There are no files associated with this item. | |||||
Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.
Edit Comment