Comparison of the Inhibition Effect of Four Inhibitors on the Corrosion Behaviour of AM60 Magnesium Alloy

IMR OpenIR

	Comparison of the Inhibition Effect of Four Inhibitors on the Corrosion Behaviour of AM60 Magnesium Alloy
	Liu, D; Song, YW; Shan, DY; Han, EH; Song, YW (reprint author), Chinese Acad Sci, Inst Met Res, Key Lab Nucl Mat & Safety Assessment, Shenyang 110016, Liaoning, Peoples R China.
	2018-03-01
发表期刊	INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE
ISSN	1452-3981
卷号	13 期号:3 页码:2219-2235
摘要	The inhibition effect of four inhibitors of sodium citrate (SC), sodium dodecylbenzenesulphonate (SDBS), diammonium phosphate ((NH4)(2)HPO4) and sodium vanadate (NaVO3) on the corrosion behaviour of AM60 magnesium alloy in 0.1 M sodium chloride (NaCl) solution was investigated by immersion and electrochemical tests, surface morphology and chemical composition analyses. The results show that AM60 suffers severe attack in NaCl solution in long-term immersion. When inhibitors are added, its corrosion resistance is improved. All these inhibitors can form a barrier to inhibit the corrosion process. Especially, the barrier becomes more protective after longer immersion. All the inhibitors except (NH4)(2)HPO4 can prevent the localized corrosion of AM60. The inhibition efficiency of organic inhibitors is better than that of inorganic inhibitors. The most efficient inhibitor is SDBS with efficiency up to 93% measured by hydrogen evolution.; The inhibition effect of four inhibitors of sodium citrate (SC), sodium dodecylbenzenesulphonate (SDBS), diammonium phosphate ((NH4)(2)HPO4) and sodium vanadate (NaVO3) on the corrosion behaviour of AM60 magnesium alloy in 0.1 M sodium chloride (NaCl) solution was investigated by immersion and electrochemical tests, surface morphology and chemical composition analyses. The results show that AM60 suffers severe attack in NaCl solution in long-term immersion. When inhibitors are added, its corrosion resistance is improved. All these inhibitors can form a barrier to inhibit the corrosion process. Especially, the barrier becomes more protective after longer immersion. All the inhibitors except (NH4)(2)HPO4 can prevent the localized corrosion of AM60. The inhibition efficiency of organic inhibitors is better than that of inorganic inhibitors. The most efficient inhibitor is SDBS with efficiency up to 93% measured by hydrogen evolution.
部门归属	[liu, dan ; song, yingwei ; shan, dayong ; han, en-hou] chinese acad sci, inst met res, key lab nucl mat & safety assessment, shenyang 110016, liaoning, peoples r china ; [liu, dan] univ sci & technol china, sch mat sci & engn, hefei 230026, anhui, peoples r china
关键词	Mg Alloy Chloride Solution Ethylene-glycol Az91d Coatings 8-hydroxyquinoline Protection Resistance Mechanism Cast
学科领域	Electrochemistry
资助者	National Natural Science Foundation of China [51671199]; National Key Research and Development Program of China [2016 YFB0301105]
收录类别	SCI
语种	英语
WOS记录号	WOS:000429101700003
引用统计	被引频次：12[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/79440
专题	中国科学院金属研究所
通讯作者	Song, YW (reprint author), Chinese Acad Sci, Inst Met Res, Key Lab Nucl Mat & Safety Assessment, Shenyang 110016, Liaoning, Peoples R China.
推荐引用方式 GB/T 7714	Liu, D,Song, YW,Shan, DY,et al. Comparison of the Inhibition Effect of Four Inhibitors on the Corrosion Behaviour of AM60 Magnesium Alloy[J]. INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE,2018,13(3):2219-2235.
APA	Liu, D,Song, YW,Shan, DY,Han, EH,&Song, YW .(2018).Comparison of the Inhibition Effect of Four Inhibitors on the Corrosion Behaviour of AM60 Magnesium Alloy.INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE,13(3),2219-2235.
MLA	Liu, D,et al."Comparison of the Inhibition Effect of Four Inhibitors on the Corrosion Behaviour of AM60 Magnesium Alloy".INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE 13.3(2018):2219-2235.