Influence of oxidation related structural defects on localized corrosion in HVAF-sprayed Fe-based metallic coatings
Wu, J; Zhang, SD; Sun, WH; Wang, JQ; Wang, JQ (reprint author), Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, Shenyang 110016, Liaoning, Peoples R China.
2018-02-15
发表期刊SURFACE & COATINGS TECHNOLOGY
ISSN0257-8972
卷号335页码:205-218
摘要Oxidation occurred in thermal spray process is an important problem deteriorating corrosion performance of thermal-sprayed Fe-based metallic coatings due to the formation of Cr-depleted zones and structural defects around the spray formed oxides. To clarify the correlation between the oxidation related structural defects formed during thermal spray process (i.e. the interparticle regions and the connected pores) and the localized corrosion, a dense Fe-based metallic coating with high Cr-content was fabricated, the long term immersion tests which continued for 30 days combined with electrochemical impedance spectroscopy measurements in 3.5 wt% NaCl were performed. It was found that electrolyte solution diffused to the inner coating through the interparticle oxide layers, and subsequently the localized corrosion developed along the interparticle oxide layers. A number of corrosion pits and corrosion channels were observed along with the interparticle oxide layers for the coating after one month immersion. Through sealing the diffusion pathways in the as-sprayed coatings by using aluminum phosphate, the corrosion resistance of the coatings was enhanced with decreased corrosion current density and improved endurance in long term immersion tests.; Oxidation occurred in thermal spray process is an important problem deteriorating corrosion performance of thermal-sprayed Fe-based metallic coatings due to the formation of Cr-depleted zones and structural defects around the spray formed oxides. To clarify the correlation between the oxidation related structural defects formed during thermal spray process (i.e. the interparticle regions and the connected pores) and the localized corrosion, a dense Fe-based metallic coating with high Cr-content was fabricated, the long term immersion tests which continued for 30 days combined with electrochemical impedance spectroscopy measurements in 3.5 wt% NaCl were performed. It was found that electrolyte solution diffused to the inner coating through the interparticle oxide layers, and subsequently the localized corrosion developed along the interparticle oxide layers. A number of corrosion pits and corrosion channels were observed along with the interparticle oxide layers for the coating after one month immersion. Through sealing the diffusion pathways in the as-sprayed coatings by using aluminum phosphate, the corrosion resistance of the coatings was enhanced with decreased corrosion current density and improved endurance in long term immersion tests.
部门归属[wu, j. ; zhang, s. d. ; sun, w. h. ; wang, j. q.] chinese acad sci, inst met res, shenyang natl lab mat sci, shenyang 110016, liaoning, peoples r china ; [wu, j.] univ sci & technol china, sch mat sci & engn, shenyang 110016, liaoning, peoples r china
关键词Constant-phase-element Electrochemical Impedance Spectroscopy Cavitation Erosion Behavior Nacl Solution Physical Interpretation Surface Distributions Amorphous Coatings Stainless-steel Water-uptake Capacitance
学科领域Materials Science, Coatings & Films ; Physics, Applied
资助者National Key Research and Development Program of China [2016YFB1100204]; National Natural Science Foundation of China [51471166, 51131006]
收录类别SCI
语种英语
文献类型期刊论文
条目标识符http://ir.imr.ac.cn/handle/321006/79499
专题中国科学院金属研究所
通讯作者Wang, JQ (reprint author), Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, Shenyang 110016, Liaoning, Peoples R China.
推荐引用方式
GB/T 7714
Wu, J,Zhang, SD,Sun, WH,et al. Influence of oxidation related structural defects on localized corrosion in HVAF-sprayed Fe-based metallic coatings[J]. SURFACE & COATINGS TECHNOLOGY,2018,335:205-218.
APA Wu, J,Zhang, SD,Sun, WH,Wang, JQ,&Wang, JQ .(2018).Influence of oxidation related structural defects on localized corrosion in HVAF-sprayed Fe-based metallic coatings.SURFACE & COATINGS TECHNOLOGY,335,205-218.
MLA Wu, J,et al."Influence of oxidation related structural defects on localized corrosion in HVAF-sprayed Fe-based metallic coatings".SURFACE & COATINGS TECHNOLOGY 335(2018):205-218.
条目包含的文件
条目无相关文件。
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[Wu, J]的文章
[Zhang, SD]的文章
[Sun, WH]的文章
百度学术
百度学术中相似的文章
[Wu, J]的文章
[Zhang, SD]的文章
[Sun, WH]的文章
必应学术
必应学术中相似的文章
[Wu, J]的文章
[Zhang, SD]的文章
[Sun, WH]的文章
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。