题名: Electrochemical Corrosion Behavior of Ferritic Steels in Molten (Li,Na,K)F
作者: Wang, YL;  Liu, HJ;  Zeng, CL;  Li, WH
发表日期: 2018-2-1
摘要: The corrosion of ferritic steels in fluoride salts limits the development of advanced molten salt reactors. In-situ electrochemical measurements for B409M and B439 were performed at 700 degrees C in molten (Li,Na,K)F by potentiodynamic polarization and electrochemical impedance spectroscopy. The experimental results indicate that the current densities for B409M and B439 are approximately 631 and 738 mu A.cm(-2), respectively. The impedance spectra plots for B409M and B439 are both composed of two capacitance loops for the duration of a 100 h experimental test. Cr-depleted corrosion layers are formed on the surface of B409M and B439 through fluoridation processes. And the corrosion mechanism is also discussed.
刊名: INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE
Appears in Collections:中国科学院金属研究所_期刊论文

Files in This Item:

There are no files associated with this item.




Recommended Citation:
Wang, YL,Liu, HJ,Zeng, CL,et al. Electrochemical Corrosion Behavior Of Ferritic Steels In Molten (li,na,k)f[J]. International Journal Of Electrochemical Science,2018,13(2):1629-1639.

SCI Citaion Data:
Service
 Recommend this item
 Sava as my favorate item
 Show this item's statistics
 Export Endnote File
Google Scholar
 Similar articles in Google Scholar
 [Wang, YL]'s Articles
 [Liu, HJ]'s Articles
 [Zeng, CL]'s Articles
CSDL cross search
 Similar articles in CSDL Cross Search
 [Wang, YL]‘s Articles
 [Liu, HJ]‘s Articles
 [Zeng, CL]‘s Articles
Scirus search
 Similar articles in Scirus
Related Copyright Policies
Null
Social Bookmarking
  Add to CiteULike  Add to Connotea  Add to Del.icio.us  Add to Digg  Add to Reddit 
所有评论 (0)
暂无评论
 
评注功能仅针对注册用户开放,请您登录
您对该条目有什么异议,请填写以下表单,管理员会尽快联系您。
内 容:
Email:  *
单位:
验证码:   刷新
您在IR的使用过程中有什么好的想法或者建议可以反馈给我们。
标 题:
 *
内 容:
Email:  *
验证码:   刷新

Items in IR are protected by copyright, with all rights reserved, unless otherwise indicated.

 

 

Valid XHTML 1.0!
Copyright © 2007-2018  中国科学院金属研究所  -Feedback
Powered by CSpace