题名: Effect of Solution Treatment on the Microstructure and Mechanical Properties of Sand-Cast Mg-9Gd-4Y-0.5Zr Alloy
作者: Li, JL;  Zhang, N;  Wang, XX;  Wu, D;  Chen, RS
发表日期: 2018-2-1
摘要: Sand-cast Mg-9Gd-4Y-0.5Zr (wt%) alloy was solution- treated at 500-565 degrees C in the time range of 0.5-30 h in air or vacuum to investigate its microstructure evolution and mechanical properties. The results showed that solution treatment temperature had a significant influence on the dissolving rate of eutectic phase and grain growth. Taken both of them into consideration, 510-520 degrees C was considered to be the optimum solution treatment temperature range for this alloy. It should be noted that the trace (0.4-0.9 vol%) and insoluble cuboid-shaped phase precipitated during solution treatment was identified to be YH2, of which the hydrogen was thought to come from both the melting and solution heating process. In addition, the 3D morphology and dissolving process of Mg-24(Gd, Y)(5) eutectic phases in the as-cast alloy were also discussed via in-situ observation under X-ray tomography.
刊名: ACTA METALLURGICA SINICA-ENGLISH LETTERS
Appears in Collections:中国科学院金属研究所_期刊论文

Files in This Item:

There are no files associated with this item.




Recommended Citation:
Li, JL,Zhang, N,Wang, XX,et al. Effect Of Solution Treatment On The Microstructure And Mechanical Properties Of Sand-cast Mg-9gd-4y-0.5zr Alloy[J]. Acta Metallurgica Sinica-english Letters,2018,31(2):189-198.

SCI Citaion Data:
Service
 Recommend this item
 Sava as my favorate item
 Show this item's statistics
 Export Endnote File
Google Scholar
 Similar articles in Google Scholar
 [Li, JL]'s Articles
 [Zhang, N]'s Articles
 [Wang, XX]'s Articles
CSDL cross search
 Similar articles in CSDL Cross Search
 [Li, JL]‘s Articles
 [Zhang, N]‘s Articles
 [Wang, XX]‘s Articles
Scirus search
 Similar articles in Scirus
Related Copyright Policies
Null
Social Bookmarking
  Add to CiteULike  Add to Connotea  Add to Del.icio.us  Add to Digg  Add to Reddit 
所有评论 (0)
暂无评论
 
评注功能仅针对注册用户开放,请您登录
您对该条目有什么异议,请填写以下表单,管理员会尽快联系您。
内 容:
Email:  *
单位:
验证码:   刷新
您在IR的使用过程中有什么好的想法或者建议可以反馈给我们。
标 题:
 *
内 容:
Email:  *
验证码:   刷新

Items in IR are protected by copyright, with all rights reserved, unless otherwise indicated.

 

 

Valid XHTML 1.0!
Copyright © 2007-2018  中国科学院金属研究所  -Feedback
Powered by CSpace