Influence of Temperature on Corrosion Behavior of 2A02 Al Alloy in Marine Atmospheric Environments
Cao, M; Liu, L; Fan, L; Yu, ZF; Li, Y; Oguzie, EE; Wang, FH; Liu, L (reprint author), Northeastern Univ, Corros & Protect Div, Shenyang Natl Lab Mat Sci, 3-11 Wenhua Rd, Shenyang 110819, Liaoning, Peoples R China.; Liu, L (reprint author), Chinese Acad Sci, Inst Met Res, Wencui Rd 62, Shenyang 110016, Liaoning, Peoples R China.
2018-02-01
发表期刊MATERIALS
ISSN1996-1944
卷号11期号:2页码:-
摘要The corrosion behavior of 2A02 Al alloy under 4 mg/cm(2) NaCl deposition at different temperatures (from 30 to 80 degrees C) has been studied. This corrosion behavior was researched using mass-gain, scanning electron microscopy-SEM, laser scanning confocal microscopy-LSCM, X-ray photoelectron spectroscopy-XPS and other techniques. The results showed and revealed that the corrosion was maximal at 60 degrees C after 200 h of exposure. The increase of temperature not only affected the solubility of oxygen gas in the thin film, but also promoted the transport of ions (such as Cl-), and the formation of protective AlO(OH), which further affects the corrosion speed.; The corrosion behavior of 2A02 Al alloy under 4 mg/cm(2) NaCl deposition at different temperatures (from 30 to 80 degrees C) has been studied. This corrosion behavior was researched using mass-gain, scanning electron microscopy-SEM, laser scanning confocal microscopy-LSCM, X-ray photoelectron spectroscopy-XPS and other techniques. The results showed and revealed that the corrosion was maximal at 60 degrees C after 200 h of exposure. The increase of temperature not only affected the solubility of oxygen gas in the thin film, but also promoted the transport of ions (such as Cl-), and the formation of protective AlO(OH), which further affects the corrosion speed.
部门归属[cao, min ; liu, li ; yu, zhongfen ; wang, fuhui] northeastern univ, corros & protect div, shenyang natl lab mat sci, 3-11 wenhua rd, shenyang 110819, liaoning, peoples r china ; [cao, min ; liu, li ; fan, lei ; yu, zhongfen ; li, ying ; wang, fuhui] chinese acad sci, inst met res, wencui rd 62, shenyang 110016, liaoning, peoples r china ; [oguzie, emeka e.] fed univ technol owerri, dept chem, electrochem & mat sci res lab, pmb 1526, owerri, nigeria
关键词Aluminum-alloys Electrochemical-behavior Pitting Corrosion Stainless-steels Nacl Solution Water-vapor Mild-steel Pure Al Chloride 2024-t3
学科领域Materials Science, Multidisciplinary
资助者National Key Basic Research and Development Plan of China [2014CB643303]; National Natural Science Fund of China [51622106]; National Key Research and Development Program of China [2017YFB0702303]
收录类别SCI
语种英语
文献类型期刊论文
条目标识符http://ir.imr.ac.cn/handle/321006/79531
专题中国科学院金属研究所
通讯作者Liu, L (reprint author), Northeastern Univ, Corros & Protect Div, Shenyang Natl Lab Mat Sci, 3-11 Wenhua Rd, Shenyang 110819, Liaoning, Peoples R China.; Liu, L (reprint author), Chinese Acad Sci, Inst Met Res, Wencui Rd 62, Shenyang 110016, Liaoning, Peoples R China.
推荐引用方式
GB/T 7714
Cao, M,Liu, L,Fan, L,et al. Influence of Temperature on Corrosion Behavior of 2A02 Al Alloy in Marine Atmospheric Environments[J]. MATERIALS,2018,11(2):-.
APA Cao, M.,Liu, L.,Fan, L.,Yu, ZF.,Li, Y.,...&Liu, L .(2018).Influence of Temperature on Corrosion Behavior of 2A02 Al Alloy in Marine Atmospheric Environments.MATERIALS,11(2),-.
MLA Cao, M,et al."Influence of Temperature on Corrosion Behavior of 2A02 Al Alloy in Marine Atmospheric Environments".MATERIALS 11.2(2018):-.
条目包含的文件
条目无相关文件。
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[Cao, M]的文章
[Liu, L]的文章
[Fan, L]的文章
百度学术
百度学术中相似的文章
[Cao, M]的文章
[Liu, L]的文章
[Fan, L]的文章
必应学术
必应学术中相似的文章
[Cao, M]的文章
[Liu, L]的文章
[Fan, L]的文章
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。