题名: The Effect of Sulfur on the Carburization of Three Fe-19Ni-21Cr-xAl (x=0, 2, 6 at.%) Alloys at 900 A degrees C in Oxygen-Contaminated CH4-H-2-H2S Atmospheres
作者: Liu, S;  Shen, J;  Guo, XH;  Niu, Y
发表日期: 2018-2-1
摘要: The effect of sulfur on the carburization of three Fe-19Ni-21Cr-xAl (x = 0, 2, 6 at.%) alloys was studied at 900 A degrees C in three CH4-H-2-H2S gases providing different sulfur pressures. For all alloys, the carbon attack decreased with an increase in the sulfur pressure, even if it was never prevented completely. However, reaction with the gas richest in H2S produced also an external chromium sulfide scale. The overall corrosion rates were slower for Fe-19Ni-21Cr-6Al than for the other two alloys under each gas mixture due to the formation of some alumina in the external scales.
刊名: OXIDATION OF METALS
Appears in Collections:中国科学院金属研究所_期刊论文

Files in This Item:

There are no files associated with this item.




Recommended Citation:
Liu, S,Shen, J,Guo, XH,et al. The Effect Of Sulfur On The Carburization Of Three Fe-19ni-21cr-xal (x=0, 2, 6 At.%) Alloys At 900 A Degrees C In Oxygen-contaminated Ch4-h-2-h2s Atmospheres[J]. Oxidation Of Metals,2018,89(43102):279-301.

SCI Citaion Data:
Service
 Recommend this item
 Sava as my favorate item
 Show this item's statistics
 Export Endnote File
Google Scholar
 Similar articles in Google Scholar
 [Liu, S]'s Articles
 [Shen, J]'s Articles
 [Guo, XH]'s Articles
CSDL cross search
 Similar articles in CSDL Cross Search
 [Liu, S]‘s Articles
 [Shen, J]‘s Articles
 [Guo, XH]‘s Articles
Scirus search
 Similar articles in Scirus
Related Copyright Policies
Null
Social Bookmarking
  Add to CiteULike  Add to Connotea  Add to Del.icio.us  Add to Digg  Add to Reddit 
所有评论 (0)
暂无评论
 
评注功能仅针对注册用户开放,请您登录
您对该条目有什么异议,请填写以下表单,管理员会尽快联系您。
内 容:
Email:  *
单位:
验证码:   刷新
您在IR的使用过程中有什么好的想法或者建议可以反馈给我们。
标 题:
 *
内 容:
Email:  *
验证码:   刷新

Items in IR are protected by copyright, with all rights reserved, unless otherwise indicated.

 

 

Valid XHTML 1.0!
Copyright © 2007-2018  中国科学院金属研究所  -Feedback
Powered by CSpace