TC25G钛合金整体叶盘锻件的组织和力学性能研究

IMR OpenIR

	TC25G钛合金整体叶盘锻件的组织和力学性能研究
其他题名	Investigation on Microstructure and Mechanical Properties of TC25G Titanium Alloy Blisk Forgings
	唐军 ; 秦卫东 ; 王清江 ; 赵子博 ; 曾卫东 ; 徐建伟
	2019
发表期刊	热加工工艺
ISSN	1001-3814
卷号	48 期号:01 页码:39-42
摘要	研究了TC25G钛合金两相区等温锻造整体叶盘的组织分布和力学性能。结果表明:锻件能顺利成形,应变分布基本均匀,没有缺陷产生。整体叶盘各部位组织均匀,呈现等轴α与片状α的双态组织形貌,初生等轴α含量约为10%,片状α相均匀地分布在β转变基体上,受两相区变形影响,α相晶界不连续,呈弯折、断裂状,可观察到部分再结晶β晶粒。TC25G钛合金整体叶盘力学性能优异,盘件各部位力学性能均满足要求,而且拉伸性能、断裂韧性、高周疲劳性能均具有较大的富余量。
其他摘要	The microstructure distribution and mechanical properties of isothermal forging TC25 G titanium alloy blisk in two phase region were studied. The results show that forgings can be formed smoothly, the strain distribution is basically uniform, and there are no defects. All parts of the blisk have uniform microstructure, which has bimodal morphologies of equiaxed α and flake α. The content of primary equiaxed α is about 10%. The lamellar α phase distributes uniformly on the transformed β matrix. Due to the effect of deformation in the two-phase region, the grain boundary of α phase is discontinuous with the form of bend or fracture, and some recrystallized β grains can be observed. The mechanical properties of TC25 G titanium alloy blisk are excellent, and the mechanical properties of all parts of the blisk meet the requirements, and the tensile properties, fracture toughness and high cycle fatigue properties all have a large surplus.
关键词	TC25G钛合金整体叶盘显微组织力学性能
学科门类	TG146.23
收录类别	CSCD
语种	中文
WOS类目	TG146.23
CSCD记录号	CSCD:6426470
引用统计
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/80396
专题	中国科学院金属研究所
作者单位	1.陕西宏远航空锻造有限责任公司 2.中国科学院金属研究所 3.西北工业大学凝固技术国家重点实验室
推荐引用方式 GB/T 7714	唐军,秦卫东,王清江,等. TC25G钛合金整体叶盘锻件的组织和力学性能研究[J]. 热加工工艺,2019,48(01):39-42.
APA	唐军,秦卫东,王清江,赵子博,曾卫东,&徐建伟.(2019).TC25G钛合金整体叶盘锻件的组织和力学性能研究.热加工工艺,48(01),39-42.
MLA	唐军,et al."TC25G钛合金整体叶盘锻件的组织和力学性能研究".热加工工艺 48.01(2019):39-42.