Hot Deformation Behavior and Processing Map of a Cu-Bearing 2205 Duplex Stainless Steel
Xi, Tong; Yin, Lu; Yang, Chun-Guang; Yang, Ke
2019-12-01
Source PublicationACTA METALLURGICA SINICA-ENGLISH LETTERS
ISSN1006-7191
Volume32Issue:12Pages:1537-1548
AbstractThe hot deformation behavior and processing map of Cu-bearing 2205 duplex stainless steel (2205-Cu DSS) were investigated at temperatures of 950-1150 degrees C and strain rates of 0.01-10 s(-1). The effects of Cu addition and different deformation parameters on deformation behavior were, respectively, characterized by analyzing flow curves, constitutive equations and microstructures. The results indicated that the shapes of flow curves strongly depended on the volume fraction of two phases. When deformed at low strain rate, DRV in ferrite was prompted with increase in the temperature and was further developed to continuous DRX. At high strain rate, flow localization preferentially occurred in ferrite at low deformation temperature due to the strain partitioning and relatively less fraction of ferrite. The activation energy for 2205-Cu DSS was 452 kJ/mol and was found to connect with the variation of strain, strain rate and deformation temperature. The optimum hot deformation parameters for 2205-Cu DSS were obtained in the temperature range of 1100-1150 degrees C and strain rate range of 0.1-1 s(-1) with a peak power dissipation efficiency of 41%. Flow localization was the main way to lead to flow instability. Meanwhile, the Cu-rich precipitates were generated within a few ferrite grains when deformed at temperature lower than 1000 degrees C. The interaction between dislocations and Cu-rich precipitates at high strain rate, as well as the limited DRV in ferrite and DRX in austenite, contributed to the complex microstructure and flow behavior.
KeywordCu-bearing duplex stainless steel Hot deformation Processing map Dynamic recrystallization Dynamic recovery
Indexed BySCI
Language英语
WOS IDWOS:000495116000011
PublisherCHINESE ACAD SCIENCES, INST METAL RESEARCH
Citation statistics
Cited Times:1[WOS]   [WOS Record]     [Related Records in WOS]
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/80592
Collection中国科学院金属研究所
Recommended Citation
GB/T 7714
Xi, Tong,Yin, Lu,Yang, Chun-Guang,et al. Hot Deformation Behavior and Processing Map of a Cu-Bearing 2205 Duplex Stainless Steel[J]. ACTA METALLURGICA SINICA-ENGLISH LETTERS,2019,32(12):1537-1548.
APA Xi, Tong,Yin, Lu,Yang, Chun-Guang,&Yang, Ke.(2019).Hot Deformation Behavior and Processing Map of a Cu-Bearing 2205 Duplex Stainless Steel.ACTA METALLURGICA SINICA-ENGLISH LETTERS,32(12),1537-1548.
MLA Xi, Tong,et al."Hot Deformation Behavior and Processing Map of a Cu-Bearing 2205 Duplex Stainless Steel".ACTA METALLURGICA SINICA-ENGLISH LETTERS 32.12(2019):1537-1548.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Xi, Tong]'s Articles
[Yin, Lu]'s Articles
[Yang, Chun-Guang]'s Articles
Baidu academic
Similar articles in Baidu academic
[Xi, Tong]'s Articles
[Yin, Lu]'s Articles
[Yang, Chun-Guang]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Xi, Tong]'s Articles
[Yin, Lu]'s Articles
[Yang, Chun-Guang]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.