Mechanical properties and wear behavior of multi-layer diamond films deposited by hot-filament chemical vapor deposition
Yan, Guangyu; Wu, Yuhou; Cristea, Daniel; Liu, Lusheng; Tierean, Mircea; Wang, Yibao; Lu, Feng; Wang, He; Yuan, Ziyao; Munteanu, Daniel; Zhao, Dehong
2019-11-15
Source PublicationAPPLIED SURFACE SCIENCE
ISSN0169-4332
Volume494Pages:401-411
AbstractDiamond films were deposited on cobalt-cemented tungsten carbide (WC-Co) by Hot-Filament Chemical Vapor Deposition (HFCVD). The mechanical properties and wear behavior of single-layer and multi-layer diamond films were compared, based on the difference of diamond crystal formation and internal structure. Adhesive failure modes and critical loads, post-scratch tests, were identified according to the applied load, acoustic emission and friction force. For single-layer diamond films, the samples produced with lower CH4 concentration evidence columnar crystal diamond structure, which exhibit better adhesive properties. The samples produced with 5% CH4 exhibit the lowest hardness, however, due to their higher crystallinity and nucleation density, they exhibit higher toughness. The multi-layer diamond film with 300 nm alternate thickness per interlayer shows the highest critical delamination load (23.22 N). Concerning the multi-layer diamond films, the hardness and Young's modulus increases from 84.13 to 94.01 GPa and 788.65 to 936.26 GPa, respectively, with the alternate thickness change from 100 nm to 600 nm per layer, which indicates that thicker alternate layers lead to higher hardness and toughness. The wear behavior of the nano-crystalline (NCD) single-layer diamond films is potentially related to the less adequate adhesive abilities to the substrate material.
KeywordHFCVD Multi-layer diamond films Adhesion Hardness Young's modulus Wear resistance
Indexed BySCI
Language英语
WOS IDWOS:000487838900046
PublisherELSEVIER
Citation statistics
Cited Times:1[WOS]   [WOS Record]     [Related Records in WOS]
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/80627
Collection中国科学院金属研究所
Recommended Citation
GB/T 7714
Yan, Guangyu,Wu, Yuhou,Cristea, Daniel,et al. Mechanical properties and wear behavior of multi-layer diamond films deposited by hot-filament chemical vapor deposition[J]. APPLIED SURFACE SCIENCE,2019,494:401-411.
APA Yan, Guangyu.,Wu, Yuhou.,Cristea, Daniel.,Liu, Lusheng.,Tierean, Mircea.,...&Zhao, Dehong.(2019).Mechanical properties and wear behavior of multi-layer diamond films deposited by hot-filament chemical vapor deposition.APPLIED SURFACE SCIENCE,494,401-411.
MLA Yan, Guangyu,et al."Mechanical properties and wear behavior of multi-layer diamond films deposited by hot-filament chemical vapor deposition".APPLIED SURFACE SCIENCE 494(2019):401-411.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Yan, Guangyu]'s Articles
[Wu, Yuhou]'s Articles
[Cristea, Daniel]'s Articles
Baidu academic
Similar articles in Baidu academic
[Yan, Guangyu]'s Articles
[Wu, Yuhou]'s Articles
[Cristea, Daniel]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Yan, Guangyu]'s Articles
[Wu, Yuhou]'s Articles
[Cristea, Daniel]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.