Tailoring microstructure and mechanical performance of the graphite-Ni based superalloy brazed combination used for molten salt reactors through thermal exposure
He, Yanming; Lu, Chuanyang; Zheng, Wenjian; Yang, Jianguo; Wang, Donghong; Shen, Hanyang; Wang, Limei; Sun, Yuan; Gao, Zengliang
2019-10-01
Source PublicationMATERIALS CHARACTERIZATION
ISSN1044-5803
Volume156
AbstractThe work investigated the effect of high- and medium-temperature thermal exposure on the microstructure and mechanical performance of the graphite/Au/Hastelloy N alloy brazed joint. The microstructure in the joint was studied with the aid of scanning electron microscope coupled with transmission electron microscope analysis. The nano-indentation was used to probe the nano-scale elastic modulus and hardness of reaction phases in the joint. The joint bond strength was evaluated by a shear test. Results indicate that: three zones (zone 1, 2 and 3) were observed in the joint with the zone 1 close to graphite while the zone 3 adjacent to Hastelloy N alloy. The precipitates in each zone were characterized and their formation mechanism was proposed. High-temperature thermal exposure was performed at 1333 K for 1-90 min. A longer soaking time facilitated the carbon diffusion and then produced a hierarchical structure with a more smooth transition of coefficient of thermal expansion, being favorable for the enhancement of the joint strength. Among the soaking time under investigation, the highest joint bond strength obtained was 34.1 MPa. Medium-temperature thermal exposure was carried out at 873-1073 K for 240 h. A high-quality joint was maintained when the joint was aged below 973 K. Over 973 K, a valid bonding was not achieved at the graphite/filler interface due to the precipitation of extensive carbon segregation in the zone 1 of the joint. The work performed will provide basic design principle for the graphite/Hastelloy N alloy brazed combinations used in molten salt reactors.
KeywordGraphite/Ni-based superalloy brazed combination Aging Transmission electron microscope Mechanical property
Indexed BySCI
Language英语
WOS IDWOS:000487565900006
PublisherELSEVIER SCIENCE INC
Citation statistics
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/80729
Collection中国科学院金属研究所
Recommended Citation
GB/T 7714
He, Yanming,Lu, Chuanyang,Zheng, Wenjian,et al. Tailoring microstructure and mechanical performance of the graphite-Ni based superalloy brazed combination used for molten salt reactors through thermal exposure[J]. MATERIALS CHARACTERIZATION,2019,156.
APA He, Yanming.,Lu, Chuanyang.,Zheng, Wenjian.,Yang, Jianguo.,Wang, Donghong.,...&Gao, Zengliang.(2019).Tailoring microstructure and mechanical performance of the graphite-Ni based superalloy brazed combination used for molten salt reactors through thermal exposure.MATERIALS CHARACTERIZATION,156.
MLA He, Yanming,et al."Tailoring microstructure and mechanical performance of the graphite-Ni based superalloy brazed combination used for molten salt reactors through thermal exposure".MATERIALS CHARACTERIZATION 156(2019).
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[He, Yanming]'s Articles
[Lu, Chuanyang]'s Articles
[Zheng, Wenjian]'s Articles
Baidu academic
Similar articles in Baidu academic
[He, Yanming]'s Articles
[Lu, Chuanyang]'s Articles
[Zheng, Wenjian]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[He, Yanming]'s Articles
[Lu, Chuanyang]'s Articles
[Zheng, Wenjian]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.