Enhanced tensile properties in a Mg-6Gd-3Y-0.5Zr alloy due to hot isostatic pressing (HIP)
Zhou, B.; Wu, D.; Chen, R. S.; Han, En-hou
2019-09-01
Source PublicationJOURNAL OF MATERIALS SCIENCE & TECHNOLOGY
ISSN1005-0302
Volume35Issue:9Pages:1860-1868
AbstractHot isostatic pressing (HIP) was applied to Mg-6Gd-3Y-0.5Zr (GW63) alloy to reduce shrinkage porosity, thus, to enhance the integrity and reliability of castings. During HIP process, shrinkage porosity was closed by grain compatible deformation and subsequent diffusion across the bonding interface. The amount of initial shrinkage porosity was the key factor for shrinkage porosity closure. HIP was testified to be effective on shrinkage porosity reduction in GW63 alloy due to its relatively narrow solidification range and resultant low content of initial shrinkage porosity in most sections, leading to higher tensile properties both in as-cast and cast-T6 condition. The improvement in tensile properties was mainly because of shrinkage porosity reduction and resultant effective rare-earth (RE) elements homogenization and precipitation strengthening. (C) 2019 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.
KeywordHot isostatic pressing Mg-Gd-Y-Zr Shrinkage porosity reduction Tensile properties
Indexed BySCI
Language英语
WOS IDWOS:000475870600007
PublisherJOURNAL MATER SCI TECHNOL
Citation statistics
Cited Times:2[WOS]   [WOS Record]     [Related Records in WOS]
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/80805
Collection中国科学院金属研究所
Recommended Citation
GB/T 7714
Zhou, B.,Wu, D.,Chen, R. S.,et al. Enhanced tensile properties in a Mg-6Gd-3Y-0.5Zr alloy due to hot isostatic pressing (HIP)[J]. JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,2019,35(9):1860-1868.
APA Zhou, B.,Wu, D.,Chen, R. S.,&Han, En-hou.(2019).Enhanced tensile properties in a Mg-6Gd-3Y-0.5Zr alloy due to hot isostatic pressing (HIP).JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,35(9),1860-1868.
MLA Zhou, B.,et al."Enhanced tensile properties in a Mg-6Gd-3Y-0.5Zr alloy due to hot isostatic pressing (HIP)".JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY 35.9(2019):1860-1868.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Zhou, B.]'s Articles
[Wu, D.]'s Articles
[Chen, R. S.]'s Articles
Baidu academic
Similar articles in Baidu academic
[Zhou, B.]'s Articles
[Wu, D.]'s Articles
[Chen, R. S.]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Zhou, B.]'s Articles
[Wu, D.]'s Articles
[Chen, R. S.]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.