Corrosion of SiO2-B2O3-Al2O3-CaF2-R2O (R = Na and K) enamels with different content of ZrO2 in H2SO4 and NaOH solutions
Chen, Ken; Chen, Minghui; Yu, Zhongdi; Wang, Qunchang; Li, Xiaoxiang; Zhu, Shenglong; Wang, Fuhui
2019-08-15
Source PublicationCERAMICS INTERNATIONAL
ISSN0272-8842
Volume45Issue:12Pages:14958-14967
AbstractCorrosion of three SiO2-B2O3-Al2O3-CaF2-R2O (R = Na and K) based enamels with different ZrO2 contents in H2SO4 and NaOH solutions was studied. The addition of ZrO2 reduced acid resistance of enamels. Especially for enamel with 5 wt% zirconia, the weight loss reached 4.04 mg/cm(2) after 30-day corrosion. On the contrary, substituting ZrO2 for SiO2 greatly improved the alkali resistance of enamel, since the weight loss of enamel with ZrO2 was only 0.3 mg/cm(2) after 20-h corrosion, which decreased to less than one third of that of enamel without ZrO2. Corrosion mechanism was comparatively discussed in these two solutions.
KeywordCorrosion Glass ZrO2
Indexed BySCI
Language英语
WOS IDWOS:000474322000059
PublisherELSEVIER SCI LTD
Citation statistics
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/80835
Collection中国科学院金属研究所
Recommended Citation
GB/T 7714
Chen, Ken,Chen, Minghui,Yu, Zhongdi,et al. Corrosion of SiO2-B2O3-Al2O3-CaF2-R2O (R = Na and K) enamels with different content of ZrO2 in H2SO4 and NaOH solutions[J]. CERAMICS INTERNATIONAL,2019,45(12):14958-14967.
APA Chen, Ken.,Chen, Minghui.,Yu, Zhongdi.,Wang, Qunchang.,Li, Xiaoxiang.,...&Wang, Fuhui.(2019).Corrosion of SiO2-B2O3-Al2O3-CaF2-R2O (R = Na and K) enamels with different content of ZrO2 in H2SO4 and NaOH solutions.CERAMICS INTERNATIONAL,45(12),14958-14967.
MLA Chen, Ken,et al."Corrosion of SiO2-B2O3-Al2O3-CaF2-R2O (R = Na and K) enamels with different content of ZrO2 in H2SO4 and NaOH solutions".CERAMICS INTERNATIONAL 45.12(2019):14958-14967.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Chen, Ken]'s Articles
[Chen, Minghui]'s Articles
[Yu, Zhongdi]'s Articles
Baidu academic
Similar articles in Baidu academic
[Chen, Ken]'s Articles
[Chen, Minghui]'s Articles
[Yu, Zhongdi]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Chen, Ken]'s Articles
[Chen, Minghui]'s Articles
[Yu, Zhongdi]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.