Temperature-gradient induced microstructure evolution in heat-affected zone of electron beam welded Ti-6Al-4V titanium alloy
Zhang, Shilin; Ma, Yingjie; Huang, Sensen; Youssef, Sabry S.; Qi, Min; Wang, Hao; Qiu, Jianke; Lei, Jiafeng; Yang, Rui
2019-08-01
Source PublicationJOURNAL OF MATERIALS SCIENCE & TECHNOLOGY
ISSN1005-0302
Volume35Issue:8Pages:1681-1690
AbstractThe heat-affected zone (HAZ) of electron beam welded (EBW) joint normally undergoes a unique heat-treating process consisting of rapid temperature rising and dropping stages, resulting in temperature-gradient in HAZ as a function of the distance to fusion zone (FZ). In the current work, microstructure, elements distribution and crystallographic orientation of three parts (near base material (BM) zone, mid-HAZ and near-FZ) in the HAZ of Ti-6Al-4V alloy were systematically investigated. The microstructure observation revealed that the microstructural variation from near-BM to near-FZ included the reduction of primary alpha (alpha(p)) grains, the increase of transformed beta structure (beta(t)) and the formation of various a structures. The rim-alpha, dendritic a and abnormal secondary alpha (alpha(s)) colonies formed in the mid-HAZ, while the "ghost" structures grew in the near-FZ respectively. The electron probe microanalyzer (EPMA) and electron back-scattered diffraction (EBSD) technologies were employed to evaluate the elements diffusion and texture evolution during the unique thermal process of welding. The formation of the various a structures in the HAZ were discussed based on the EPMA and EBSD results. Finally, the nanoindentation hardness of "ghost" structures was presented and compared with nearby beta(t) regions. (C) 2019 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.
KeywordTi-6Al-4V Electron beam welding HAZ Element distribution Texture
Indexed BySCI
Language英语
WOS IDWOS:000470677300020
PublisherJOURNAL MATER SCI TECHNOL
Citation statistics
Cited Times:6[WOS]   [WOS Record]     [Related Records in WOS]
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/80883
Collection中国科学院金属研究所
Recommended Citation
GB/T 7714
Zhang, Shilin,Ma, Yingjie,Huang, Sensen,et al. Temperature-gradient induced microstructure evolution in heat-affected zone of electron beam welded Ti-6Al-4V titanium alloy[J]. JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,2019,35(8):1681-1690.
APA Zhang, Shilin.,Ma, Yingjie.,Huang, Sensen.,Youssef, Sabry S..,Qi, Min.,...&Yang, Rui.(2019).Temperature-gradient induced microstructure evolution in heat-affected zone of electron beam welded Ti-6Al-4V titanium alloy.JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,35(8),1681-1690.
MLA Zhang, Shilin,et al."Temperature-gradient induced microstructure evolution in heat-affected zone of electron beam welded Ti-6Al-4V titanium alloy".JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY 35.8(2019):1681-1690.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Zhang, Shilin]'s Articles
[Ma, Yingjie]'s Articles
[Huang, Sensen]'s Articles
Baidu academic
Similar articles in Baidu academic
[Zhang, Shilin]'s Articles
[Ma, Yingjie]'s Articles
[Huang, Sensen]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Zhang, Shilin]'s Articles
[Ma, Yingjie]'s Articles
[Huang, Sensen]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.