The oxidation of two ternary Ni-Cu-10 at.% Al alloys in 1 atm of pure O-2 at 800-900 degrees C | |
Xiang, JH; Gesmundo, F; Niu, Y | |
通讯作者 | Niu, Y() |
2004-08-01 | |
发表期刊 | CORROSION SCIENCE
![]() |
ISSN | 0010-938X |
卷号 | 46期号:8页码:2025-2039 |
摘要 | The oxidation of the ternary alloys Ni-45Cu-10Al and Ni-30Cu-10Al has been studied at 800-900 degreesC under 1 atm O-2. The presence of 10 at.% Al reduces significantly the oxidation rate of the corresponding Cu-Ni alloys during the initial oxidation stages, even before the establishment of a complete Al2O3 layer. The weight of individual sample of the two ternary NiCu-10Al alloys at 800 degreesC increases more rapidly than at 900 degreesC during the initial oxidation stage. As oxidation proceeds, the weight gain at 800 degreesC slows down to a degree that the total weight gain after 24 h oxidation at 800 degreesC is less than that at 900 degreesC. Due to a faster formation of the Al2O3 layer, which suppresses earlier the further oxidation of Cu and Ni, the external region of the scales grown on Ni-45Cu-10Al contain much less Cu and Ni oxides than those grown on Ni-30Cu-10Al. The transition from the internal oxidation to the selective external oxidation of the most reactive component Al in Ni-Cu-Al alloys is favored by higher values of the Al content, of temperature and of the Cu/Ni ratio. (C) 2003 Elsevier Ltd. All rights reserved. |
关键词 | ternary alloys nickel-copper base oxidation aluminium effect |
DOI | 10.1016/j.corsci.2003.10.020 |
收录类别 | SCI |
语种 | 英语 |
WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
WOS类目 | Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering |
WOS记录号 | WOS:000222843300014 |
出版者 | PERGAMON-ELSEVIER SCIENCE LTD |
引用统计 | |
文献类型 | 期刊论文 |
条目标识符 | http://ir.imr.ac.cn/handle/321006/80956 |
通讯作者 | Niu, Y |
作者单位 | 1.Chinese Acad Sci, Inst Met Res, State Key Lab Corros & Protect, Shenyang 110016, Peoples R China 2.Univ Genoa, Dipartimento Ingn Chim, I-16129 Genoa, Italy |
推荐引用方式 GB/T 7714 | Xiang, JH,Gesmundo, F,Niu, Y. The oxidation of two ternary Ni-Cu-10 at.% Al alloys in 1 atm of pure O-2 at 800-900 degrees C[J]. CORROSION SCIENCE,2004,46(8):2025-2039. |
APA | Xiang, JH,Gesmundo, F,&Niu, Y.(2004).The oxidation of two ternary Ni-Cu-10 at.% Al alloys in 1 atm of pure O-2 at 800-900 degrees C.CORROSION SCIENCE,46(8),2025-2039. |
MLA | Xiang, JH,et al."The oxidation of two ternary Ni-Cu-10 at.% Al alloys in 1 atm of pure O-2 at 800-900 degrees C".CORROSION SCIENCE 46.8(2004):2025-2039. |
条目包含的文件 | 条目无相关文件。 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论