EFFECT OF Mn PRE-PARTITIONING ON C PARTITIONING AND RETAINED AUSTENITE OF Q&P STEELS
Chen Liansheng1; Zhang Jianyang1; Tian Yaqiang1; Song Jinying1; Xu Yong1,2; Zhang Shihong2
通讯作者Chen Liansheng(kyc@heuu.edu.cn)
2015-05-11
发表期刊ACTA METALLURGICA SINICA
ISSN0412-1961
卷号51期号:5页码:527-536
摘要The chemical compositions of C and Mn have a strong influence on the stability of the metastable retained austenite at room temperature. In the intercritical annealing process, Mn element improves the stability of the austenite by partitioning from ferrite to austenite and the enrichment of Mn in austenite can also impact on the diffusion of C element from martensite to retained austenite in partitioning process. Based on C partitioning, Mn partitioning can further improve the product of strength and elongation, and has no negative effect on weldability of the low carbon high strength steel. Thus, it can effectively solve the contradiction between mechanical property and weldability of low carbon high strength steel in traditional quenching-partitioning (Q&P) process. In this case, it is of great significance to study the Mn pre-partitioning mechanism and its influence on C partitioning and retained austenite of the low carbon high strength steel. Therefore, one low alloy C-Si-Mn steel was studied in the present work. The Mn pre-partitioning behavior and its effect on C partitioning and the stability of the retained austenite were investigated by means of intercritical heating-quenching (IQ) process, Q&P and intercritical heating-austenitizing-quenching-partitioning (I&Q&P) process. The results showed that during the process of phase transformation in the intercritical reheating, C and Mn elements constantly diffused from ferrite to austenite. When this process ended, C and Mn elements enriched in austenite. While Mn element in microstructure at room temperature was still enrichment and C element enriched regularly between the martensite laths in the I&Q&P treated steel. With the increase of C partitioning time in both Q&P and I&Q&P process, the tensile strength of steel was decreased constantly, while the elongation showed an increasing fristly and then decreasing trend. The product of strength and elongation of the steel treated by I&Q&P process reached 23478 MPa % with the C partitioning time of 90 s. The more austenite in martensite phase would be obtained after the first quenching with the Mn pre-partitioning. It was important to prompt more C diffusing into austenite during C partitioning process to stabilize more retained austenite at room temperature of the steel after the second quenching. With the same experimental conditions, the retained austenite of the combined effects of C and Mn partitioning during I&Q&P process would be increased 2.4% than the effect of C partitioning during Q&P process.
关键词Mn partitioning C partitioning retained austenite product of strength and elongation
资助者National Natural Science Foundation of China ; Natural Science Foundation of Hebei Province ; Science Foundation of Department of Education of Hebei Province
收录类别SCI
语种英语
资助项目National Natural Science Foundation of China[51254004] ; National Natural Science Foundation of China[51304186] ; Natural Science Foundation of Hebei Province[E2014209191] ; Science Foundation of Department of Education of Hebei Province[YQ2013003]
WOS研究方向Metallurgy & Metallurgical Engineering
WOS类目Metallurgy & Metallurgical Engineering
WOS记录号WOS:000355388000003
出版者SCIENCE PRESS
引用统计
文献类型期刊论文
条目标识符http://ir.imr.ac.cn/handle/321006/81063
通讯作者Chen Liansheng
作者单位1.Hebei United Univ, Hebei Key Lab Modern Met Technol, Tangshan 063009, Peoples R China
2.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China
推荐引用方式
GB/T 7714
Chen Liansheng,Zhang Jianyang,Tian Yaqiang,et al. EFFECT OF Mn PRE-PARTITIONING ON C PARTITIONING AND RETAINED AUSTENITE OF Q&P STEELS[J]. ACTA METALLURGICA SINICA,2015,51(5):527-536.
APA Chen Liansheng,Zhang Jianyang,Tian Yaqiang,Song Jinying,Xu Yong,&Zhang Shihong.(2015).EFFECT OF Mn PRE-PARTITIONING ON C PARTITIONING AND RETAINED AUSTENITE OF Q&P STEELS.ACTA METALLURGICA SINICA,51(5),527-536.
MLA Chen Liansheng,et al."EFFECT OF Mn PRE-PARTITIONING ON C PARTITIONING AND RETAINED AUSTENITE OF Q&P STEELS".ACTA METALLURGICA SINICA 51.5(2015):527-536.
条目包含的文件
条目无相关文件。
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[Chen Liansheng]的文章
[Zhang Jianyang]的文章
[Tian Yaqiang]的文章
百度学术
百度学术中相似的文章
[Chen Liansheng]的文章
[Zhang Jianyang]的文章
[Tian Yaqiang]的文章
必应学术
必应学术中相似的文章
[Chen Liansheng]的文章
[Zhang Jianyang]的文章
[Tian Yaqiang]的文章
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。