Development and oxidation at 800 degrees C of a novel electrodeposited Ni-Cr nanocomposite film
Zhang, Y; Peng, X; Wang, F
通讯作者Peng, X()
2004-02-01
发表期刊MATERIALS LETTERS
ISSN0167-577X
卷号58期号:6页码:1134-1138
摘要A novel Ni-9.6 wt.% Cr nanocomposite film was prepared by co-electrodeposition of Ni and Cr nanoparticles in an average size of 39 nm. The Cr natroparticles were dispersed in the electrodeposited nanocrystalline Ni grains (31 nm in average). The oxidation at 800 degreesC showed that the as-deposited Ni-Cr nanocomposite film has a superior oxidation resistance compared to the electrodeposited pure Ni film and the uncoated Ni matrix. X-ray diffraction characterization and cross-sectional investigation indicated that a continuous Cr2O3 scale formed on the electrodeposited nanocomposite film. (C) 2003 Elsevier B.V. All rights reserved.
关键词electrodeposition oxidation Ni-Cr nanocomposite film
DOI10.1016/j.matlet.2003.09.006
收录类别SCI
语种英语
WOS研究方向Materials Science ; Physics
WOS类目Materials Science, Multidisciplinary ; Physics, Applied
WOS记录号WOS:000188288600060
出版者ELSEVIER SCIENCE BV
引用统计
文献类型期刊论文
条目标识符http://ir.imr.ac.cn/handle/321006/81103
通讯作者Peng, X
作者单位Chinese Acad Sci, Inst Met Res, State Key Lab Corros & Protect, Shenyang 110016, Peoples R China
推荐引用方式
GB/T 7714
Zhang, Y,Peng, X,Wang, F. Development and oxidation at 800 degrees C of a novel electrodeposited Ni-Cr nanocomposite film[J]. MATERIALS LETTERS,2004,58(6):1134-1138.
APA Zhang, Y,Peng, X,&Wang, F.(2004).Development and oxidation at 800 degrees C of a novel electrodeposited Ni-Cr nanocomposite film.MATERIALS LETTERS,58(6),1134-1138.
MLA Zhang, Y,et al."Development and oxidation at 800 degrees C of a novel electrodeposited Ni-Cr nanocomposite film".MATERIALS LETTERS 58.6(2004):1134-1138.
条目包含的文件
条目无相关文件。
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[Zhang, Y]的文章
[Peng, X]的文章
[Wang, F]的文章
百度学术
百度学术中相似的文章
[Zhang, Y]的文章
[Peng, X]的文章
[Wang, F]的文章
必应学术
必应学术中相似的文章
[Zhang, Y]的文章
[Peng, X]的文章
[Wang, F]的文章
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。