	Powder coated route for production of SiCf/Ti precursor fiber
	Li, YS; Shi, NL; Zhang, DZ; Yang, R
通讯作者	Yang, R()
	2004-05-11
发表期刊	ACTA METALLURGICA SINICA
ISSN	0412-1961
卷号	40 期号:5 页码:551-554
摘要	In making Sic precursor fiber using a powder coated route, the binder, poly (methyl methacrylate) was used, and the solvent is acetone. The viscosity of the binder was tested by viscometer, and the critical concentration of the binder is 0.03 g/mL. The content of residual substance of the binder at different temperatures and pressures was test by chemical analysis. The volatility kinetics of the binder was also studied. The temperature for the binder decomposition is about 230 degreesC, the velocity reaches its maximum at about 350 degreesC, and the decomposition completed under 400 degreesC. The decomposition and transgression velocities increase when temperature is increased under the same pressure. The transgression velocity reduces when pressure is increased at the same temperature. The process of making uniform precursor was found by a uniformity design method.
关键词	(SiCfTi)-Ti-/ precursor fiber powder coated route binder
收录类别	SCI
语种	英语
WOS研究方向	Metallurgy & Metallurgical Engineering
WOS类目	Metallurgy & Metallurgical Engineering
WOS记录号	WOS:000221838900022
出版者	SCIENCE CHINA PRESS
引用统计
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/81274
通讯作者	Yang, R
作者单位	Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China
推荐引用方式 GB/T 7714	Li, YS,Shi, NL,Zhang, DZ,et al. Powder coated route for production of SiCf/Ti precursor fiber[J]. ACTA METALLURGICA SINICA,2004,40(5):551-554.
APA	Li, YS,Shi, NL,Zhang, DZ,&Yang, R.(2004).Powder coated route for production of SiCf/Ti precursor fiber.ACTA METALLURGICA SINICA,40(5),551-554.
MLA	Li, YS,et al."Powder coated route for production of SiCf/Ti precursor fiber".ACTA METALLURGICA SINICA 40.5(2004):551-554.