Corrosion of enamel with and without CaF2 in molten aluminum at 750 degrees C
Yu, Zhongdi; Chen, Minghui; Chen, Ken; Xie, Dongbai; Zhu, Shenglong; Wang, Fuhui
2019-03-01
Source PublicationCORROSION SCIENCE
ISSN0010-938X
Volume148Pages:228-236
AbstractCoatings and bulks of enamel with and without CaF2 were prepared to investigate their corrosion behavior in molten Al at 750 degrees C. Enamel coatings provide high corrosion resistance to the 304 stainless steel against molten Al. In the presence of 2.5 wt% CaF2, its corrosion resistance was further improved. Detail study on corrosion of the enamel bulks reveals that such role of CaF2 played on the corrosion behavior of enamel relies on the following two aspects: (1) Concentration of fluorides at surface reduces wettability; (2) Adding CaF2 changes crystallization of enamel, and different crystallites result in the varied corrosion resistance.
KeywordStainless steel Enamel High temperature corrosion Molten aluminum
Indexed BySCI
Language英语
WOS IDWOS:000457950400022
PublisherPERGAMON-ELSEVIER SCIENCE LTD
Citation statistics
Cited Times:1[WOS]   [WOS Record]     [Related Records in WOS]
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/81327
Collection中国科学院金属研究所
Recommended Citation
GB/T 7714
Yu, Zhongdi,Chen, Minghui,Chen, Ken,et al. Corrosion of enamel with and without CaF2 in molten aluminum at 750 degrees C[J]. CORROSION SCIENCE,2019,148:228-236.
APA Yu, Zhongdi,Chen, Minghui,Chen, Ken,Xie, Dongbai,Zhu, Shenglong,&Wang, Fuhui.(2019).Corrosion of enamel with and without CaF2 in molten aluminum at 750 degrees C.CORROSION SCIENCE,148,228-236.
MLA Yu, Zhongdi,et al."Corrosion of enamel with and without CaF2 in molten aluminum at 750 degrees C".CORROSION SCIENCE 148(2019):228-236.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Yu, Zhongdi]'s Articles
[Chen, Minghui]'s Articles
[Chen, Ken]'s Articles
Baidu academic
Similar articles in Baidu academic
[Yu, Zhongdi]'s Articles
[Chen, Minghui]'s Articles
[Chen, Ken]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Yu, Zhongdi]'s Articles
[Chen, Minghui]'s Articles
[Chen, Ken]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.