Microstructure and mechanical properties of a new cast nickel-based superalloy K4750 joint produced by gas tungsten arc welding process
Xie, Jilin; Ma, Yingche; Xing, Weiwei; Ou, Meiqiong; Zhang, Long; Liu, Kui
2019-02-01
Source PublicationJOURNAL OF MATERIALS SCIENCE
ISSN0022-2461
Volume54Issue:4Pages:3558-3571
AbstractThe microstructures and mechanical properties of gas tungsten arc-welded joints of superalloy K4750 that has been newly developed were examined. The microsegregation pattern during solidification of the fusion zone indicated that Fe was prone to segregate into the dendritic core, while Nb, Mo, Ti, W and Si were rejected into the dendritic boundary. The phase transformation sequence of the K4750 alloy fusion zone was LL+L+ +(Ti,Nb)C+(Ti,Nb)C. Heat-affected zone (HAZ) examination shows it consisted of partially melted zone with liquated MC carbides and liquated grain boundaries. Cracking-free HAZ microstructure suggested that K4750 alloy possess excellent HAZ cracking resistance properties. Relatively low concentration of Al and Ti results in the excellent cracking resistance properties of the alloy. Vickers microhardness of as-welded joint is lower than that of post-weld heat treatment (PWHT) joint across the whole joint due to the absence of 50nm spherical particles formed during PWHT. Tensile properties of as-welded joints are comparable to PWHT joints in terms of the ultimate tensile strength and elongation.
Indexed BySCI
Language英语
WOS IDWOS:000452502500063
PublisherSPRINGER
Citation statistics
Cited Times:3[WOS]   [WOS Record]     [Related Records in WOS]
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/81423
Collection中国科学院金属研究所
Recommended Citation
GB/T 7714
Xie, Jilin,Ma, Yingche,Xing, Weiwei,et al. Microstructure and mechanical properties of a new cast nickel-based superalloy K4750 joint produced by gas tungsten arc welding process[J]. JOURNAL OF MATERIALS SCIENCE,2019,54(4):3558-3571.
APA Xie, Jilin,Ma, Yingche,Xing, Weiwei,Ou, Meiqiong,Zhang, Long,&Liu, Kui.(2019).Microstructure and mechanical properties of a new cast nickel-based superalloy K4750 joint produced by gas tungsten arc welding process.JOURNAL OF MATERIALS SCIENCE,54(4),3558-3571.
MLA Xie, Jilin,et al."Microstructure and mechanical properties of a new cast nickel-based superalloy K4750 joint produced by gas tungsten arc welding process".JOURNAL OF MATERIALS SCIENCE 54.4(2019):3558-3571.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Xie, Jilin]'s Articles
[Ma, Yingche]'s Articles
[Xing, Weiwei]'s Articles
Baidu academic
Similar articles in Baidu academic
[Xie, Jilin]'s Articles
[Ma, Yingche]'s Articles
[Xing, Weiwei]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Xie, Jilin]'s Articles
[Ma, Yingche]'s Articles
[Xing, Weiwei]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.