Breakaway oxidation of a low-Al content nanocrystalline coating at 1000 degrees C
Sun, Wenyao; Chen, Minghui; Bao, Zebin; Wu, Changjun; Zhu, Shenglong; Wang, Fuihui
2019-01-25
Source PublicationSURFACE & COATINGS TECHNOLOGY
ISSN0257-8972
Volume358Pages:958-967
AbstractNanocrystalline coating though with low Al reservoir shows high oxidation and spallation resistance, owing to its high density of defects and grain boundaries. It now attracts growing attention. However, with oxidation going on, its stability is always a significant concern since such a high-temperature protective coating should be designed with a long life-expectancy when the nano-sized grains have grown and the reserved Al has been consumed a lot. Yet, this issue has never been clarified. To identify the exact mode of breakaway oxidation, a nanocrystalline coating was prepared with very low Al content that could decrease fast to a critical value in a very short oxidation time. Its oxidation behaviour related with the stability was studied in detail at 1000 degrees C. Results indicate that an intact external alumina scale still forms at the surface of the nanocrystalline coating initially. However, after 100 h exposure, grains growing and the continuous consuming of Al of the nanocrystalline coating lead to oxidation of Ti and doping of titanium oxide in the alumina scale, which was accompanied with the formation of abundant micropores and cracks. Thereafter, scale spalls off and abundant less-protective oxides, e.g. TiO2, NiCr2O4, NiTiO3, form, and breakaway oxidation occurs.
KeywordSuperalloys Nanocrystalline coating High-temperature oxidation
Indexed BySCI
Language英语
WOS IDWOS:000456762300113
PublisherELSEVIER SCIENCE SA
Citation statistics
Cited Times:1[WOS]   [WOS Record]     [Related Records in WOS]
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/81437
Collection中国科学院金属研究所
Recommended Citation
GB/T 7714
Sun, Wenyao,Chen, Minghui,Bao, Zebin,et al. Breakaway oxidation of a low-Al content nanocrystalline coating at 1000 degrees C[J]. SURFACE & COATINGS TECHNOLOGY,2019,358:958-967.
APA Sun, Wenyao,Chen, Minghui,Bao, Zebin,Wu, Changjun,Zhu, Shenglong,&Wang, Fuihui.(2019).Breakaway oxidation of a low-Al content nanocrystalline coating at 1000 degrees C.SURFACE & COATINGS TECHNOLOGY,358,958-967.
MLA Sun, Wenyao,et al."Breakaway oxidation of a low-Al content nanocrystalline coating at 1000 degrees C".SURFACE & COATINGS TECHNOLOGY 358(2019):958-967.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Sun, Wenyao]'s Articles
[Chen, Minghui]'s Articles
[Bao, Zebin]'s Articles
Baidu academic
Similar articles in Baidu academic
[Sun, Wenyao]'s Articles
[Chen, Minghui]'s Articles
[Bao, Zebin]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Sun, Wenyao]'s Articles
[Chen, Minghui]'s Articles
[Bao, Zebin]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.