Antibacterial TiCu/TiCuN Multilayer Films with Good Corrosion Resistance Deposited by Axial Magnetic Field-Enhanced Arc Ion Plating
Peng, Cong; Zhao, Yanhui; Jin, Shujing; Wang, JingRen; Liu, Rui; Liu, Hui; Shi, Wenbo; Kolawole, Sharafadeen Kunle; Ren, Ling; Yu, Baohai; Yang, Ke
2019-01-09
Source PublicationACS APPLIED MATERIALS & INTERFACES
ISSN1944-8244
Volume11Issue:1Pages:125-136
AbstractIn order to develop a novel kind of antibacterial Cu-containing TiN film with good corrosion resistance, impressive mechanical properties, and low cytotoxicity, three differently designed multilayer films of TiCu/TiCuN multilayer (M1, M2, M3) were deposited on the surface of 316L stainless steel surface using the axial magnetic field-enhanced arc ion plating (AMFE-ARP) method, in which the interlayer of TiCu was first introduced for Cu-containing TiN film in order to improve comprehensive properties, especially the corrosion resistance of the film. The performance of the TiCu/TiCuN multilayer films was compared with that of the two single layers, TiN and TiCuN, which were deposited by the same method and the same total deposition time. The results indicated that the TiCu/TiCuN multilayer film of M2 revealed the best comprehensive corrosion resistance with low electric current values, high pitting potential, and high polarization resistance due to the proper thickness of TiCu interlayers and larger number of TiCu/TiCuN bilayers. In addition, the TiCu/TiCuN multilayer film of M2 also possesses comparable mechanical properties, excellent antibacterial and antibiofilm abilities, as well as good biocompatibility. Consequently, the antibacterial TiCu/TiCuN multilayer films with good corrosion resistance deposited by using the axial magnetic field-enhanced arc ion plating (AMFE-ARP) method are promising for application in biomedical antibacterial film for implants.
KeywordTiCu/TiCuN multilayer coating arc ion plating antibacterial property corrosion resistance
Indexed BySCI
Language英语
WOS IDWOS:000455561200016
PublisherAMER CHEMICAL SOC
Citation statistics
Cited Times:11[WOS]   [WOS Record]     [Related Records in WOS]
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/81464
Collection中国科学院金属研究所
Recommended Citation
GB/T 7714
Peng, Cong,Zhao, Yanhui,Jin, Shujing,et al. Antibacterial TiCu/TiCuN Multilayer Films with Good Corrosion Resistance Deposited by Axial Magnetic Field-Enhanced Arc Ion Plating[J]. ACS APPLIED MATERIALS & INTERFACES,2019,11(1):125-136.
APA Peng, Cong.,Zhao, Yanhui.,Jin, Shujing.,Wang, JingRen.,Liu, Rui.,...&Yang, Ke.(2019).Antibacterial TiCu/TiCuN Multilayer Films with Good Corrosion Resistance Deposited by Axial Magnetic Field-Enhanced Arc Ion Plating.ACS APPLIED MATERIALS & INTERFACES,11(1),125-136.
MLA Peng, Cong,et al."Antibacterial TiCu/TiCuN Multilayer Films with Good Corrosion Resistance Deposited by Axial Magnetic Field-Enhanced Arc Ion Plating".ACS APPLIED MATERIALS & INTERFACES 11.1(2019):125-136.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Peng, Cong]'s Articles
[Zhao, Yanhui]'s Articles
[Jin, Shujing]'s Articles
Baidu academic
Similar articles in Baidu academic
[Peng, Cong]'s Articles
[Zhao, Yanhui]'s Articles
[Jin, Shujing]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Peng, Cong]'s Articles
[Zhao, Yanhui]'s Articles
[Jin, Shujing]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.