Improving the oxidation resistance of Ti3SiC2 by forming a Ti3Si0.9Al0.1C2 solid solution
Zhang, HB; Zhou, YC; Bao, YW; Li, MS
通讯作者Zhou, YC()
2004-07-12
发表期刊ACTA MATERIALIA
ISSN1359-6454
卷号52期号:12页码:3631-3637
摘要The oxidation behavior of the Ti3Si0.9Al0.1C2 solid solution in air was investigated at 1000-1350 degreesC. The parabolic rate constants of Ti3Si0.9Al0.1C2 were decreased by 2-4 orders of magnitude compared with those of Ti3SiC2 at 1000-1300 degreesC. At 1000-1100 degreesC, the oxide scales displayed a continuous alpha-Al-2-O-3 inner layer and a discontinuous TiO2 (rutile) outer layer. At 1200-1300 degreesC, the continuous inner layer was still alpha-Al2O3, but the outer layer was a mixture of TiO2 (rutile) and Al2TiO5. The oxide layers were dense, adherent and resistant to thermal cycling. However, the oxidation resistance of Ti3Si0.9Al0.1C2 deteriorated at 1350 degreesC because of the depletion of alpha-Al2O3. This depletion was caused by the extensive reaction between TiO2 (rutile) and alpha-Al2O3 to form Al2TiO5. The high activity and diffusion of Al and the low solubility of oxygen in the solid solution were the key factors for the formation of a continuous alpha-Al2O3 layer during high-temperature oxidation. (C) 2004 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
关键词ceramics oxidation layered structures activity solid solution
DOI10.1016/j.actamat.2004.04.015
收录类别SCI
语种英语
WOS研究方向Materials Science ; Metallurgy & Metallurgical Engineering
WOS类目Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering
WOS记录号WOS:000222707800023
出版者PERGAMON-ELSEVIER SCIENCE LTD
引用统计
文献类型期刊论文
条目标识符http://ir.imr.ac.cn/handle/321006/81892
通讯作者Zhou, YC
作者单位Chinese Acad Sci, Shenyang Natl Lab Mat Sci, Inst Met Res, Shenyang 110016, Peoples R China
推荐引用方式
GB/T 7714
Zhang, HB,Zhou, YC,Bao, YW,et al. Improving the oxidation resistance of Ti3SiC2 by forming a Ti3Si0.9Al0.1C2 solid solution[J]. ACTA MATERIALIA,2004,52(12):3631-3637.
APA Zhang, HB,Zhou, YC,Bao, YW,&Li, MS.(2004).Improving the oxidation resistance of Ti3SiC2 by forming a Ti3Si0.9Al0.1C2 solid solution.ACTA MATERIALIA,52(12),3631-3637.
MLA Zhang, HB,et al."Improving the oxidation resistance of Ti3SiC2 by forming a Ti3Si0.9Al0.1C2 solid solution".ACTA MATERIALIA 52.12(2004):3631-3637.
条目包含的文件
条目无相关文件。
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[Zhang, HB]的文章
[Zhou, YC]的文章
[Bao, YW]的文章
百度学术
百度学术中相似的文章
[Zhang, HB]的文章
[Zhou, YC]的文章
[Bao, YW]的文章
必应学术
必应学术中相似的文章
[Zhang, HB]的文章
[Zhou, YC]的文章
[Bao, YW]的文章
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。