Oxidation of a novel chromium coating with CeO2 dispersions
Zhu, L; Peng, X; Yan, J; Wang, F
通讯作者Peng, X(xpeng@imr.ac.cn)
2004-12-01
发表期刊OXIDATION OF METALS
ISSN0030-770X
卷号62期号:5-6页码:411-426
摘要Chromium coatings have been in widespread use to enhance the high-temperature oxidation resistance of low-alloy steely since the 1950s [Samuel and Lockington, Metal Treatment and Drop forgeing 18, 354 (1951); Sully and Brandes, Chromium, 2nd edn. Butterworths, London 1967]. In this work, a novel CeO2-dispersed chromium coating with a fine-grain structure was manufactured on a mild-carbon steel by Prior composite electrodeposition of Ni with CeO2 particles, followed by chromizing using a conventional halide activate, pack-cementation method. For comparison, chromizing was also performed on the carbon steel and on the one with Ni-plating pretreatment. Cyclic oxidation at 840degreesC for 120 h showed that among the three various samples chromized, the CeO2-dispersed chromium coating exhibited the best oxidation resistance, while the worst for the coating on the carbon steel The samples after oxidation were investigated using X-ray diffraction (XRD), scanning-electron microscopy equipped with energy dispersive X-ray analysis (SEMI/EDAX) and electron-probe microanalysis (EPMA). The results indicated that although all three coatings grew chromia scales during oxidation, the one formed on the CeO2-modified coating Was thinner, denser and had a fine-grain structured Moreover, the formation of "Kirkendall" voids and new precipitates, which occurred during oxidation below the scale in the chromium coating on the Ni-plated sample, was prevented in the presence of CeO2 particles in the coating The CeO2 effects on the coating formation and the coating oxidation behavior are discussed in detail.
关键词electrodepostion chromizing CeO2-dispersed chromizing coating mild-carbon steel high-temperature oxidation reactive-element effect
收录类别SCI
语种英语
WOS研究方向Metallurgy & Metallurgical Engineering
WOS类目Metallurgy & Metallurgical Engineering
WOS记录号WOS:000226001700007
出版者KLUWER ACADEMIC/PLENUM PUBL
引用统计
文献类型期刊论文
条目标识符http://ir.imr.ac.cn/handle/321006/81978
通讯作者Peng, X
作者单位Chinese Acad Sci, Inst Met Res, State Key Lab Corros & Protect, Shenyang 110016, Peoples R China
推荐引用方式
GB/T 7714
Zhu, L,Peng, X,Yan, J,et al. Oxidation of a novel chromium coating with CeO2 dispersions[J]. OXIDATION OF METALS,2004,62(5-6):411-426.
APA Zhu, L,Peng, X,Yan, J,&Wang, F.(2004).Oxidation of a novel chromium coating with CeO2 dispersions.OXIDATION OF METALS,62(5-6),411-426.
MLA Zhu, L,et al."Oxidation of a novel chromium coating with CeO2 dispersions".OXIDATION OF METALS 62.5-6(2004):411-426.
条目包含的文件
条目无相关文件。
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[Zhu, L]的文章
[Peng, X]的文章
[Yan, J]的文章
百度学术
百度学术中相似的文章
[Zhu, L]的文章
[Peng, X]的文章
[Yan, J]的文章
必应学术
必应学术中相似的文章
[Zhu, L]的文章
[Peng, X]的文章
[Yan, J]的文章
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。