Failure analysis of corrosion cracking and simulated testing for a fluid catalytic cracking unit | |
Chen, H; Li, XG; Dong, CF; Li, M; Yang, JW | |
通讯作者 | Li, XG(lixiaogang99@263.net) |
2005-04-01 | |
发表期刊 | JOURNAL OF UNIVERSITY OF SCIENCE AND TECHNOLOGY BEIJING
![]() |
ISSN | 1005-8850 |
卷号 | 12期号:2页码:172-177 |
摘要 | The failure of a fluid catalysis and cracking unit (FCCU) in a Chinese refinery was investigated by using nondestructive detection methods, fracture surface examination, hardness measurement, chemical composition and corrosion products analysis. The results showed that the failure was caused by the dew point nitrate stress corrosion cracking. For a long operation period, the wall temperature of the regenerator in the FCCU was below the fume dew point. As a result, an acid fume NOx-SOx-H2O medium presented on the surface, resulting in stress corrosion cracking of the component with high residual stress. In order to confirm the relative conclusion, simulated testing was conducted in laboratory, and the results showed similar cracking characteristics. Finally, some suggestions have been made to prevent the stress corrosion cracking of an FCCU from re-occurring in the future. |
关键词 | stress corrosion cracking fluid catalytic cracking unit dew point failure |
收录类别 | SCI |
语种 | 英语 |
WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering ; Mining & Mineral Processing |
WOS类目 | Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering ; Mining & Mineral Processing |
WOS记录号 | WOS:000228698500015 |
出版者 | JOURNAL OF UNIV OF SCIENCE AND TECHNOLOGY BEIJING |
引用统计 | |
文献类型 | 期刊论文 |
条目标识符 | http://ir.imr.ac.cn/handle/321006/82014 |
通讯作者 | Li, XG |
作者单位 | 1.Univ Sci & Technol Beijing, Sch Mat Sci & Engn, Beijing 100083, Peoples R China 2.Chinese Acad Sci, Inst Met Res, State Key Lab Corros & Prot, Shenyang 110016, Peoples R China 3.Jiujiang Branch Corp, SINOPEC, Jiujiang 332000, Peoples R China |
推荐引用方式 GB/T 7714 | Chen, H,Li, XG,Dong, CF,et al. Failure analysis of corrosion cracking and simulated testing for a fluid catalytic cracking unit[J]. JOURNAL OF UNIVERSITY OF SCIENCE AND TECHNOLOGY BEIJING,2005,12(2):172-177. |
APA | Chen, H,Li, XG,Dong, CF,Li, M,&Yang, JW.(2005).Failure analysis of corrosion cracking and simulated testing for a fluid catalytic cracking unit.JOURNAL OF UNIVERSITY OF SCIENCE AND TECHNOLOGY BEIJING,12(2),172-177. |
MLA | Chen, H,et al."Failure analysis of corrosion cracking and simulated testing for a fluid catalytic cracking unit".JOURNAL OF UNIVERSITY OF SCIENCE AND TECHNOLOGY BEIJING 12.2(2005):172-177. |
条目包含的文件 | 条目无相关文件。 |
个性服务 |
推荐该条目 |
保存到收藏夹 |
查看访问统计 |
导出为Endnote文件 |
谷歌学术 |
谷歌学术中相似的文章 |
[Chen, H]的文章 |
[Li, XG]的文章 |
[Dong, CF]的文章 |
百度学术 |
百度学术中相似的文章 |
[Chen, H]的文章 |
[Li, XG]的文章 |
[Dong, CF]的文章 |
必应学术 |
必应学术中相似的文章 |
[Chen, H]的文章 |
[Li, XG]的文章 |
[Dong, CF]的文章 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论