Thermal stability of structure and hardness of the surface layer of 316L stainless steel after surface mechanical attrition treatment | |
Wang, AX; Liu, G; Zhou, L; Wang, K; Yang, XH; Li, Y | |
通讯作者 | Liu, G() |
2005-06-01 | |
发表期刊 | ACTA METALLURGICA SINICA
![]() |
ISSN | 0412-1961 |
卷号 | 41期号:6页码:577-582 |
摘要 | After surface mechanical attrition treatment (SMAT) for 316L stainless steel, a gradient structure in its surface layer with grain size from nano-scale to micro-scale was obtained. The samples before and after the SMAT were annealed in vacuum at different temperatures for different durations, and the structural evolution as well as the hardness and the residual stress variations along the depth were analyzed. Experimental results show that when the annealing temperature is lower than 0.5T(m) (T-m is the melt point), no obvious change can be found for the grain size in the gradient structure, except the martensite transformation in the affected layer due to the release of residual stress, and the hardness distribution along the depth remains unchanged. When the annealing temperature is higher than 0.51(m), recovery, recrystallization and sharp drop of the residual stress occur in the gradient structure, which induce significant reduction of the hardness along the depth. The effect of annealing duration on the structure and property of the SMAT sample is less important comparing with the annealing temperature. |
关键词 | 316L stainless steel surface nanocrystallization annealing structure hardness |
收录类别 | SCI |
语种 | 英语 |
WOS研究方向 | Metallurgy & Metallurgical Engineering |
WOS类目 | Metallurgy & Metallurgical Engineering |
WOS记录号 | WOS:000230238800004 |
出版者 | SCIENCE PRESS |
引用统计 | |
文献类型 | 期刊论文 |
条目标识符 | http://ir.imr.ac.cn/handle/321006/82354 |
通讯作者 | Liu, G |
作者单位 | 1.Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, Shenyang 110016, Peoples R China 2.Fuzhou Univ, Sch Mat Sci & Engn, Fuzhou 350002, Peoples R China 3.Chinese Acad Sci, Inst Met Res, State Key Lab Corros & Protect, Shenyang 110016, Peoples R China |
推荐引用方式 GB/T 7714 | Wang, AX,Liu, G,Zhou, L,et al. Thermal stability of structure and hardness of the surface layer of 316L stainless steel after surface mechanical attrition treatment[J]. ACTA METALLURGICA SINICA,2005,41(6):577-582. |
APA | Wang, AX,Liu, G,Zhou, L,Wang, K,Yang, XH,&Li, Y.(2005).Thermal stability of structure and hardness of the surface layer of 316L stainless steel after surface mechanical attrition treatment.ACTA METALLURGICA SINICA,41(6),577-582. |
MLA | Wang, AX,et al."Thermal stability of structure and hardness of the surface layer of 316L stainless steel after surface mechanical attrition treatment".ACTA METALLURGICA SINICA 41.6(2005):577-582. |
条目包含的文件 | 条目无相关文件。 |
个性服务 |
推荐该条目 |
保存到收藏夹 |
查看访问统计 |
导出为Endnote文件 |
谷歌学术 |
谷歌学术中相似的文章 |
[Wang, AX]的文章 |
[Liu, G]的文章 |
[Zhou, L]的文章 |
百度学术 |
百度学术中相似的文章 |
[Wang, AX]的文章 |
[Liu, G]的文章 |
[Zhou, L]的文章 |
必应学术 |
必应学术中相似的文章 |
[Wang, AX]的文章 |
[Liu, G]的文章 |
[Zhou, L]的文章 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论