Effects of pre-oxidation on the corrosion behavior of pure Ti under coexistence of solid NaCl deposit and humid oxygen at 600 degrees C: the diffusion of chlorine
Fan, Lei; Liu, Li; Lv, Yuhai; Wang, Hao; Fu, Anqing; Yuan, Juntao; Li, Ying; Wang, Fuhui; Yin, Chengxian
2020-10-01
Source PublicationSCIENTIFIC REPORTS
Volume10Issue:1
AbstractThe effect of pre-oxidation on the corrosion behavior of pure Ti covered with a solid NaCl deposit in the humid O-2 flow at 600 degrees C is studied. The oxide scale, formed by pre-oxidation, protects the substrate from the NaCl induced corrosion during the initial stage. However, the corrosion of the pre-oxidized sample is severely accelerated by solid NaCl after an incubation period. The chlorine, generated from the decomposition of solid NaCl, diffuses into the oxide/substrate interface as ions during the incubation period, which was observed by ToF-SIMS. The chlorine at the oxide/substrate interface induces the fast corrosion after the incubation period although the pre-oxidation scale is complete and compact.
DOI10.1038/s41598-020-73034-y
WOS IDWOS:000577143400054
Citation statistics
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/82468
Collection中国科学院金属研究所
Recommended Citation
GB/T 7714
Fan, Lei,Liu, Li,Lv, Yuhai,et al. Effects of pre-oxidation on the corrosion behavior of pure Ti under coexistence of solid NaCl deposit and humid oxygen at 600 degrees C: the diffusion of chlorine[J]. SCIENTIFIC REPORTS,2020,10(1).
APA Fan, Lei.,Liu, Li.,Lv, Yuhai.,Wang, Hao.,Fu, Anqing.,...&Yin, Chengxian.(2020).Effects of pre-oxidation on the corrosion behavior of pure Ti under coexistence of solid NaCl deposit and humid oxygen at 600 degrees C: the diffusion of chlorine.SCIENTIFIC REPORTS,10(1).
MLA Fan, Lei,et al."Effects of pre-oxidation on the corrosion behavior of pure Ti under coexistence of solid NaCl deposit and humid oxygen at 600 degrees C: the diffusion of chlorine".SCIENTIFIC REPORTS 10.1(2020).
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Fan, Lei]'s Articles
[Liu, Li]'s Articles
[Lv, Yuhai]'s Articles
Baidu academic
Similar articles in Baidu academic
[Fan, Lei]'s Articles
[Liu, Li]'s Articles
[Lv, Yuhai]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Fan, Lei]'s Articles
[Liu, Li]'s Articles
[Lv, Yuhai]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.