Effect of rolling temperature on microstructure and mechanical properties of Ti/steel clad plates fabricated by cold spraying and hot-rolling
Zhao, Zhipo; Tang, Junrong; Tariq, Naeem ul Haq; Liu, Housheng; Liu, Hanhui; Ren, Yupeng; Tong, Min; Yin, Lisong; Du, Hao; Wang, Jiqiang; Xiong, Tianying
2020-09-23
Source PublicationMATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
Volume795
AbstractThe effect of rolling temperature on the interfacial microstructure and mechanical properties of Ti/steel clad plates, fabricated by a newly designed method (cold spraying and hot-rolling), was studied. For this purpose, three rolling temperatures (i.e. 850, 950, 1050 degrees C) were selected to completely understand the bonding mechanism at Ti/steel interface. The type of interfacial compounds and thickness of the diffusion layers were found to be the main factors controlling the mechanical properties of the Ti/steel clad plates. Results showed that the Ti/steel clad plate rolled at 850 degrees C exhibited metallurgical bonding due to the formation of a 250 nm thick TiC diffusion layer at the interface, and resulted in the best elongation. In contrast, the sample rolled at 950 degrees C developed a 400 nm thick diffusion layer which was composed of TiC and FeTi compounds, leading to the best tensile strength. When the rolling temperature was increased to 1050 degrees C, the thickness of the diffusion layer (composed of coarse TiC and FeTi phases) was sharply increased to 4 mu m, and the sample displayed poor tensile strength and elongation.
DOI10.1016/j.msea.2020.139982
WOS IDWOS:000576174400003
Citation statistics
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/82514
Collection中国科学院金属研究所
Recommended Citation
GB/T 7714
Zhao, Zhipo,Tang, Junrong,Tariq, Naeem ul Haq,et al. Effect of rolling temperature on microstructure and mechanical properties of Ti/steel clad plates fabricated by cold spraying and hot-rolling[J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,2020,795.
APA Zhao, Zhipo.,Tang, Junrong.,Tariq, Naeem ul Haq.,Liu, Housheng.,Liu, Hanhui.,...&Xiong, Tianying.(2020).Effect of rolling temperature on microstructure and mechanical properties of Ti/steel clad plates fabricated by cold spraying and hot-rolling.MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,795.
MLA Zhao, Zhipo,et al."Effect of rolling temperature on microstructure and mechanical properties of Ti/steel clad plates fabricated by cold spraying and hot-rolling".MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING 795(2020).
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Zhao, Zhipo]'s Articles
[Tang, Junrong]'s Articles
[Tariq, Naeem ul Haq]'s Articles
Baidu academic
Similar articles in Baidu academic
[Zhao, Zhipo]'s Articles
[Tang, Junrong]'s Articles
[Tariq, Naeem ul Haq]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Zhao, Zhipo]'s Articles
[Tang, Junrong]'s Articles
[Tariq, Naeem ul Haq]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.