Exfoliation corrosion behavior of T6 treated 2090 Al-Li alloy in EXCO solution, and EIS during exfoliation corrosion evolution

IMR OpenIR

	Exfoliation corrosion behavior of T6 treated 2090 Al-Li alloy in EXCO solution, and EIS during exfoliation corrosion evolution
	Su, JX ; Zhang, Z ; Cao, FH ; Zhang, JQ ; Cao, CN
通讯作者	Su, JX(sujingxin@hotmail.com)
	2005-09-01
发表期刊	ACTA METALLURGICA SINICA
ISSN	0412-1961
卷号	41 期号:9 页码:974-978
摘要	Electrochemical impedance spectroscopy (EIS) and in situ microscopic image of T6 peak-aged AA2090 Al-Li alloys in EXCO solution were studied. The localized corrosion form of the alloy during immersion evolved from pitting through intergranular corrosion, exfoliation corrosion (EC) to post EC. EC initiated at big corrosion pits which were formed with inclusion phase as center in pitting stage. The EC blisters propagate from these big pits till the upper layer is totally lifted. EIS of the initiation stage of pitting corrosion consists of a high frequency capacitive arc and a middle-low frequency inductive arc, and the inductive arc tends to disappear when pitting corrosion starts to propagate. In the intergranular corrosion stage, the second time constant corresponding to the corroded area can hardly be distinguished in the capacitive part of the EIS. In the stages of EC propagation and post EC, their EIS consist of two capacitive arcs.
关键词	Al-Li alloy electrochemical impedance spectroscopy (EIS) EXCO solution exfoliation corrosion
收录类别	SCI
语种	英语
WOS研究方向	Metallurgy & Metallurgical Engineering
WOS类目	Metallurgy & Metallurgical Engineering
WOS记录号	WOS:000232503700014
出版者	SCIENCE PRESS
引用统计	被引频次：4[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/82561
专题	中国科学院金属研究所
通讯作者	Su, JX
作者单位	1.Zhejiang Univ, Dept Chem, Hangzhou 310027, Peoples R China 2.Chinese Acad Sci, Inst Met Res, State Key Lab Corros & Protect, Shenyang 110016, Peoples R China
推荐引用方式 GB/T 7714	Su, JX,Zhang, Z,Cao, FH,et al. Exfoliation corrosion behavior of T6 treated 2090 Al-Li alloy in EXCO solution, and EIS during exfoliation corrosion evolution[J]. ACTA METALLURGICA SINICA,2005,41(9):974-978.
APA	Su, JX,Zhang, Z,Cao, FH,Zhang, JQ,&Cao, CN.(2005).Exfoliation corrosion behavior of T6 treated 2090 Al-Li alloy in EXCO solution, and EIS during exfoliation corrosion evolution.ACTA METALLURGICA SINICA,41(9),974-978.
MLA	Su, JX,et al."Exfoliation corrosion behavior of T6 treated 2090 Al-Li alloy in EXCO solution, and EIS during exfoliation corrosion evolution".ACTA METALLURGICA SINICA 41.9(2005):974-978.