Corrosion inhibitor performances for carbon dioxide corrosion of N80 steel under static and flowing conditions
Jiang, X; Zheng, YG; Ke, W
通讯作者Zheng, YG()
2005-04-01
发表期刊CORROSION
ISSN0010-9312
卷号61期号:4页码:326-334
摘要Inhibition for carbon dioxide (CO2) corrosion of N80 steel by quaternary alkynoxymethyl amine (IMC-80-Q) in 3% sodium chloride (NaCl) solution was investigated under static and flowing conditions using a modified rotating disk apparatus. The effects of flow velocity and concentration of inhibitor on inhibition performance were performed using a weight-loss test, scanning electron microscope (SEM) observation, and electrochemical techniques including electrochemical impedance spectroscopy (EIS), linear polarization resistance, and polarization curves. The results showed that flow velocity had strong effects on the inhibitor performances. Inhibition efficiency (q) and polarization resistance (R) exhibited the peak-value phenomenon at an inhibitor concentration of 150 mg/L when flow velocity was less than 5 m/s, in contrast with the 300 mg/L when flow velocity was higher than 5 m/s. Critical flow velocity in the uninhibited solution was between 4 m/s and 5 m/s.
关键词carbon dioxide corrosion criticalflow velocity flow effect inhibitor N80 steel peak-value phenomenon
收录类别SCI
语种英语
WOS研究方向Materials Science ; Metallurgy & Metallurgical Engineering
WOS类目Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering
WOS记录号WOS:000228235600003
出版者NATL ASSN CORROSION ENG
引用统计
文献类型期刊论文
条目标识符http://ir.imr.ac.cn/handle/321006/82852
通讯作者Zheng, YG
作者单位Chinese Acad Sci, Met Res Inst, State Key Lab Corros & Protect, Shenyang 110016, Liaoning Prov, Peoples R China
推荐引用方式
GB/T 7714
Jiang, X,Zheng, YG,Ke, W. Corrosion inhibitor performances for carbon dioxide corrosion of N80 steel under static and flowing conditions[J]. CORROSION,2005,61(4):326-334.
APA Jiang, X,Zheng, YG,&Ke, W.(2005).Corrosion inhibitor performances for carbon dioxide corrosion of N80 steel under static and flowing conditions.CORROSION,61(4),326-334.
MLA Jiang, X,et al."Corrosion inhibitor performances for carbon dioxide corrosion of N80 steel under static and flowing conditions".CORROSION 61.4(2005):326-334.
条目包含的文件
条目无相关文件。
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[Jiang, X]的文章
[Zheng, YG]的文章
[Ke, W]的文章
百度学术
百度学术中相似的文章
[Jiang, X]的文章
[Zheng, YG]的文章
[Ke, W]的文章
必应学术
必应学术中相似的文章
[Jiang, X]的文章
[Zheng, YG]的文章
[Ke, W]的文章
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。