Phase stability of TiAl-X (X=V, Nb, Ta, Cr, Mo, W, and Mn) alloys
Ye, Li-Hua; Wang, Hao; Zhou, Gang; Hu, Qing-Miao; Yang, Rui
2020-04-05
Source PublicationJOURNAL OF ALLOYS AND COMPOUNDS
Volume819
AbstractIntroducing high symmetric cubic disordered beta or ordered beta(0) phases by alloying beta-stabilizers improves the strength and high-temperature deformability of intermetallic gamma-TiAl. However, the beta phase is prone to decomposition of lower symmetric hexagonal phases such as omega(0) and omega '', which are extremely brittle and harmful to the ductility of the alloy. Therefore, understanding the effect of the beta-stabilizers on the phase stability of TiAl is crucial for the rational design of TiAl based alloys. In the present work, the equilibrium lattice structures, bulk moduli, and heats of formation of beta, beta(0), omega '', and omega(0) of TiAl with some typical beta stabilizers V, Nb, Ta, Cr, Mo, W, and Mn were calculated by using a first-principles method, with which the relative phase stability were discussed. We showed that the phase stability sequence is beta < beta(0) < omega(0) < omega '' for Ti4Al3Nb and Ti4Al3Ta, beta < beta(0) < omega(0) < omega '' for Ti4Al3V, Ti4Al3Mo and Ti4Al3W, and beta < beta(0) < omega(0) < omega '' for Ti4Al3Cr and Ti4Al3Mn. The beta-stabilizing effect of the alloying element X increases from Nb/Ta to V/Mo/W to Cr/Mn. The relative stability of the various phases is roughly in accordance with the trends of the unit volume and bulk modulus against the phases with a few exceptions. The phase diagrams of the alloys associated with these phases were estimated by comparing the free energies against the temperature of various phases, evaluated with the calculated unit volumes and bulk moduli. (C) 2019 Elsevier B.V. All rights reserved.
DOI10.1016/j.jallcom.2019.153291
WOS IDWOS:000507378300070
Citation statistics
Cited Times:5[WOS]   [WOS Record]     [Related Records in WOS]
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/82968
Collection中国科学院金属研究所
Recommended Citation
GB/T 7714
Ye, Li-Hua,Wang, Hao,Zhou, Gang,et al. Phase stability of TiAl-X (X=V, Nb, Ta, Cr, Mo, W, and Mn) alloys[J]. JOURNAL OF ALLOYS AND COMPOUNDS,2020,819.
APA Ye, Li-Hua,Wang, Hao,Zhou, Gang,Hu, Qing-Miao,&Yang, Rui.(2020).Phase stability of TiAl-X (X=V, Nb, Ta, Cr, Mo, W, and Mn) alloys.JOURNAL OF ALLOYS AND COMPOUNDS,819.
MLA Ye, Li-Hua,et al."Phase stability of TiAl-X (X=V, Nb, Ta, Cr, Mo, W, and Mn) alloys".JOURNAL OF ALLOYS AND COMPOUNDS 819(2020).
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Ye, Li-Hua]'s Articles
[Wang, Hao]'s Articles
[Zhou, Gang]'s Articles
Baidu academic
Similar articles in Baidu academic
[Ye, Li-Hua]'s Articles
[Wang, Hao]'s Articles
[Zhou, Gang]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Ye, Li-Hua]'s Articles
[Wang, Hao]'s Articles
[Zhou, Gang]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.