A novel laminated metal composite with superior interfacial bonding composed of ultrahigh-strength maraging steel and 316L stainless steel
Zhang, Le; Wang, Wei; Shahzad, M.; Shan, Yi-yin; Yang, Ke
2020-04-01
Source PublicationJOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL
Volume27Issue:4Pages:433-439
AbstractA 5-layer laminated metal composite composed of ultrahigh-strength maraging steel and ductile 316L stainless steel was fabricated by hot pressing in vacuum and post-heat treatment. Microstructure characterization on hierarchical structure of the composite before and after heat treatment was made by optical microscopy, scanning electron microscopy and electron back-scattered diffraction technique, respectively. Meanwhile, the difference of mechanical performance on both sides of the interface was characterized by nano-hardness testing. Uniaxial tensile test showed that superior interfacial bonding was achieved due to the micro-'bite' structure between the two steels without obvious defects or oxides at the interface and with coordinated deformation of the two components. Thus, a laminated metal composite consisting of two different constituents with extreme difference in strength can be well fabricated.
DOI10.1007/s42243-020-00382-4
WOS IDWOS:000522174900001
Citation statistics
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/83014
Collection中国科学院金属研究所
Recommended Citation
GB/T 7714
Zhang, Le,Wang, Wei,Shahzad, M.,et al. A novel laminated metal composite with superior interfacial bonding composed of ultrahigh-strength maraging steel and 316L stainless steel[J]. JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL,2020,27(4):433-439.
APA Zhang, Le,Wang, Wei,Shahzad, M.,Shan, Yi-yin,&Yang, Ke.(2020).A novel laminated metal composite with superior interfacial bonding composed of ultrahigh-strength maraging steel and 316L stainless steel.JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL,27(4),433-439.
MLA Zhang, Le,et al."A novel laminated metal composite with superior interfacial bonding composed of ultrahigh-strength maraging steel and 316L stainless steel".JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL 27.4(2020):433-439.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Zhang, Le]'s Articles
[Wang, Wei]'s Articles
[Shahzad, M.]'s Articles
Baidu academic
Similar articles in Baidu academic
[Zhang, Le]'s Articles
[Wang, Wei]'s Articles
[Shahzad, M.]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Zhang, Le]'s Articles
[Wang, Wei]'s Articles
[Shahzad, M.]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.