Temperature Effects on the Microstructures of Mg-Gd-Y Alloy Processed by Multi-direction Impact Forging
Shah, S. S. A.; Wu, D.; Chen, R. S.; Song, G. S.
2020-02-01
Source PublicationACTA METALLURGICA SINICA-ENGLISH LETTERS
Volume33Issue:2Pages:243-251
AbstractA high strain rate multi-directional impact forging (MDIF) was applied to a solutionized Mg-Gd-Y-Zr alloy in the temperature range of 350-500 degrees C. Results demonstrate that the dominant deformation mode is twinning at a temperature below 400 degrees C, whereas at a medium temperature of 450 degrees C considerable continuous dynamic recrystallization was promoted by {10-12} extension twins. At a higher temperature of 500 degrees C, twinning activation was suppressed. New DRX grains were observed but their sizes were much bigger than those resulting from the MDIFed 50 passes at 450 degrees C, which are ascribed to the larger grain boundary mobility and atomic diffusion at 500 degrees C. Moreover, a non-basal weak texture was gained afterward MDIF at each temperature, which is credited to the MDIF process and the minor strain applied in each pass.
DOI10.1007/s40195-019-00972-6
WOS IDWOS:000519309400002
Citation statistics
Cited Times:1[WOS]   [WOS Record]     [Related Records in WOS]
Document Type期刊论文
Identifierhttp://ir.imr.ac.cn/handle/321006/83170
Collection中国科学院金属研究所
Recommended Citation
GB/T 7714
Shah, S. S. A.,Wu, D.,Chen, R. S.,et al. Temperature Effects on the Microstructures of Mg-Gd-Y Alloy Processed by Multi-direction Impact Forging[J]. ACTA METALLURGICA SINICA-ENGLISH LETTERS,2020,33(2):243-251.
APA Shah, S. S. A.,Wu, D.,Chen, R. S.,&Song, G. S..(2020).Temperature Effects on the Microstructures of Mg-Gd-Y Alloy Processed by Multi-direction Impact Forging.ACTA METALLURGICA SINICA-ENGLISH LETTERS,33(2),243-251.
MLA Shah, S. S. A.,et al."Temperature Effects on the Microstructures of Mg-Gd-Y Alloy Processed by Multi-direction Impact Forging".ACTA METALLURGICA SINICA-ENGLISH LETTERS 33.2(2020):243-251.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Shah, S. S. A.]'s Articles
[Wu, D.]'s Articles
[Chen, R. S.]'s Articles
Baidu academic
Similar articles in Baidu academic
[Shah, S. S. A.]'s Articles
[Wu, D.]'s Articles
[Chen, R. S.]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Shah, S. S. A.]'s Articles
[Wu, D.]'s Articles
[Chen, R. S.]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.