Thixoforming of spray deposited AlZn12Cu2Mg2 wrought aluminum alloy in semi-solid state

IMR OpenIR

	Thixoforming of spray deposited AlZn12Cu2Mg2 wrought aluminum alloy in semi-solid state
	Du, ZM ; Cheng, YS ; Zhao, JZ
通讯作者	Du, ZM(duzm@263.net)
	2005-04-01
发表期刊	TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA
ISSN	1003-6326
卷号	15 页码:152-156
摘要	The processing parameters were achieved about the thixoforming of spray deposition AlZnl(2)Cu(2)Mg(2) wrought aluminum alloy in semi-solid ingots and the structures and mechanical properties of the analogue work pieces were tested. The optimum heat treatment parameters of the alloy by the optimization experiment were obtained (460 &DEG; C being the optimum solution temperature and 12-14 h being the optimum artificial aging time). The results show that AlZn12Cu2Mg2 alloy can achieve ideal mechanical properties and elongation after solution treatment and aging treatment by semi-solid process. Under 120 MPa and at 595-600 &DEG; C, the yield strength and elongation of the heat-treated parts can reach 664 MPa and 7.5% respectively.
关键词	AlZn12Cu2Mg2 alloy thixoforming spray deposition semi solid process
收录类别	SCI
语种	英语
WOS研究方向	Metallurgy & Metallurgical Engineering
WOS类目	Metallurgy & Metallurgical Engineering
WOS记录号	WOS:000228957000034
出版者	ALLERTON PRESS INC
引用统计
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/83394
专题	中国科学院金属研究所
通讯作者	Du, ZM
作者单位	1.Harbin Inst Technol, Sch Mat Sci & Engn, Harbin 150001, Peoples R China 2.Chinese Acad Sci, Met Res Inst, Shenyang 110016, Peoples R China
推荐引用方式 GB/T 7714	Du, ZM,Cheng, YS,Zhao, JZ. Thixoforming of spray deposited AlZn12Cu2Mg2 wrought aluminum alloy in semi-solid state[J]. TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA,2005,15:152-156.
APA	Du, ZM,Cheng, YS,&Zhao, JZ.(2005).Thixoforming of spray deposited AlZn12Cu2Mg2 wrought aluminum alloy in semi-solid state.TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA,15,152-156.
MLA	Du, ZM,et al."Thixoforming of spray deposited AlZn12Cu2Mg2 wrought aluminum alloy in semi-solid state".TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA 15(2005):152-156.