TEM observation of annealing microstructure of deformed Al-Mg-Sc-Zr alloy

IMR OpenIR

	TEM observation of annealing microstructure of deformed Al-Mg-Sc-Zr alloy
	Zhao, WT; Yan, DS; Rong, LJ
通讯作者	Rong, LJ()
	2005-11-01
发表期刊	ACTA METALLURGICA SINICA
ISSN	0412-1961
卷号	41 期号:11 页码:1150-1154
摘要	Al-6Mg-0.4Mn-0.2Sc-0.1Zr-0.1Cr (mass fraction, %) alloy was prepared by vacuum induction melting, and the microstructures and mechanical properties of cold worked samples annealed at 350, 400, 450 and 500 degrees C for 1 h were investigated. TEM observation indicated that tangled dislocation cells are typical microstructure in cold worked sample; After 350 degrees C annealing, the dislocations arrange regularly and the density decreases sharply, the alloy recovers partly and the grain size is about 500 nm; Further annealing to 500 degrees C, recrystallization proceeds gradually in a wide temperature range due to the Zener drag effect of Al-3 (Sc, Zr) phase. As a result, the mechanical property changes greatly at 350 degrees C but keeps steady with further temperature increasing.
关键词	Al-Mg base alloy annealing temperature Al-3(SC, Zr) subgrain boundary dislocation recrystallization
收录类别	SCI
语种	英语
WOS研究方向	Metallurgy & Metallurgical Engineering
WOS类目	Metallurgy & Metallurgical Engineering
WOS记录号	WOS:000233702000006
出版者	SCIENCE PRESS
引用统计	被引频次：7[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/83876
专题	中国科学院金属研究所
通讯作者	Rong, LJ
作者单位	Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China
推荐引用方式 GB/T 7714	Zhao, WT,Yan, DS,Rong, LJ. TEM observation of annealing microstructure of deformed Al-Mg-Sc-Zr alloy[J]. ACTA METALLURGICA SINICA,2005,41(11):1150-1154.
APA	Zhao, WT,Yan, DS,&Rong, LJ.(2005).TEM observation of annealing microstructure of deformed Al-Mg-Sc-Zr alloy.ACTA METALLURGICA SINICA,41(11),1150-1154.
MLA	Zhao, WT,et al."TEM observation of annealing microstructure of deformed Al-Mg-Sc-Zr alloy".ACTA METALLURGICA SINICA 41.11(2005):1150-1154.