Saturation dislocation microstructures of double-slip-oriented copper single crystal during the corrosion fatigue in a 0.5 mol/L NaCl aqueous solution

IMR OpenIR

	Saturation dislocation microstructures of double-slip-oriented copper single crystal during the corrosion fatigue in a 0.5 mol/L NaCl aqueous solution
	Yang, JH ; Zhang, XP ; Mai, YW ; Jia, WP ; Li, SX ; Ke, W
通讯作者	Yang, JH(jihong.yang@aeromech.usyd.edu.au)
	2005-05-01
发表期刊	JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY
ISSN	1005-0302
卷号	21 期号:3 页码:343-346
摘要	Copper single crystal specimens with the longitudinal axis parallel to the [013] clouble-slip-orientation were grown through Bridgman technique. The fatigue tests were performed using a symmetric tension-compression load mode at room temperature in an open-air and a 0.5 mol/L NaCl solution, respectively. The dislocation microstructures were observed with scanning electron microscopy (SEM) by the electron channeling contrast (ECC) and transmission electron microscopy (TEM). The results show that the saturation dislocation microstructures during the corrosion fatigue in the aqueous solution of 0.5 mol/L NaCl, mainly consisted of labyrinth, wall and vein dislocation structures, which differs from the dislocation structures of the walls and veins in an open-air environment.
关键词	double-slip-oriented copper single crystal dislocation rnicrostructures corrosion fatigue
收录类别	SCI
语种	英语
WOS研究方向	Materials Science ; Metallurgy & Metallurgical Engineering
WOS类目	Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering
WOS记录号	WOS:000229594400012
出版者	JOURNAL MATER SCI TECHNOL
引用统计
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/84664
专题	中国科学院金属研究所
通讯作者	Yang, JH
作者单位	1.Shenyang Normal Univ, Coll Phys & Technol, Shenyang 110034, Peoples R China 2.Univ Sydney, Sch Aerosp Mech & Mech Engn, Ctr Adv Mat Technol, Sydney, NSW 2006, Australia 3.Chinese Acad Sci, Met Res Inst, Shenyang 110016, Peoples R China
推荐引用方式 GB/T 7714	Yang, JH,Zhang, XP,Mai, YW,et al. Saturation dislocation microstructures of double-slip-oriented copper single crystal during the corrosion fatigue in a 0.5 mol/L NaCl aqueous solution[J]. JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,2005,21(3):343-346.
APA	Yang, JH,Zhang, XP,Mai, YW,Jia, WP,Li, SX,&Ke, W.(2005).Saturation dislocation microstructures of double-slip-oriented copper single crystal during the corrosion fatigue in a 0.5 mol/L NaCl aqueous solution.JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,21(3),343-346.
MLA	Yang, JH,et al."Saturation dislocation microstructures of double-slip-oriented copper single crystal during the corrosion fatigue in a 0.5 mol/L NaCl aqueous solution".JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY 21.3(2005):343-346.