| Fatigue behavior comparison of ecaped Al-Cu alloy under stress and strain control |
| Li, YJ; Liu, SM; Wu, SD; Zhang, ZF; Wang, ZG
|
| 通讯作者 | Zhang, ZF()
|
| 2005-04-11
|
| 发表期刊 | ACTA METALLURGICA SINICA
 |
| ISSN | 0412-1961
|
| 卷号 | 41期号:4页码:380-384 |
| 摘要 | Fatigue life, surface deformation morphology, fatigue cracking and fatigue fractography of Al-0.7%Cu (mass fraction) alloy, produced by equal channel angular pressing (ECAP) for 4 passes, were investigated under constant stress or plastic strain control. It is shown that the specimens displayed obvious cyclic softening, which caused some difference in fatigue life at low or high stress range under constant stress and strain conditions. The plastic strain is carried either by shear bands only, or by shear bands and deformation bands, in the specimens fatigued under strain control. Consequently, fatigue cracks nucleated either along shear bands or along deformation bands. However, the plastic strain only localized in the shear bands of the specimens under stress control, as a result, leading to shearing fatigue cracking. The fatigue fractography consists of several different zones, including fatigue crack initiation, slow, fast propagation and final fracture. |
| 关键词 | equal channel angular pressing (ECAP)
Al-0.7%Cu alloy
cyclic softening
shear bands
fatigue
|
| 收录类别 | SCI
|
| 语种 | 英语
|
| WOS研究方向 | Metallurgy & Metallurgical Engineering
|
| WOS类目 | Metallurgy & Metallurgical Engineering
|
| WOS记录号 | WOS:000228756900009
|
| 出版者 | SCIENCE CHINA PRESS
|
| 引用统计 |
|
| 文献类型 | 期刊论文
|
| 条目标识符 | http://ir.imr.ac.cn/handle/321006/84836
|
| 专题 | 中国科学院金属研究所
|
| 通讯作者 | Zhang, ZF |
| 作者单位 | Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, Shenyang 110016, Peoples R China
|
推荐引用方式
GB/T 7714 |
Li, YJ,Liu, SM,Wu, SD,et al. Fatigue behavior comparison of ecaped Al-Cu alloy under stress and strain control[J]. ACTA METALLURGICA SINICA,2005,41(4):380-384.
|
| APA |
Li, YJ,Liu, SM,Wu, SD,Zhang, ZF,&Wang, ZG.(2005).Fatigue behavior comparison of ecaped Al-Cu alloy under stress and strain control.ACTA METALLURGICA SINICA,41(4),380-384.
|
| MLA |
Li, YJ,et al."Fatigue behavior comparison of ecaped Al-Cu alloy under stress and strain control".ACTA METALLURGICA SINICA 41.4(2005):380-384.
|
修改评论