Oxidation and corrosion behavior of titanium aluminum nitride coatings by arc ion plating

IMR OpenIR

	Oxidation and corrosion behavior of titanium aluminum nitride coatings by arc ion plating
	Li Ming-sheng ; Feng Chang-jie ; Zhang Zhi-feng ; Wang Fu-hui
通讯作者	Li Ming-sheng(mshli@163.com)
	2006-09-01
发表期刊	TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA
ISSN	1003-6326
卷号	16 页码:S75-S80
摘要	Composite metastable TiN and Ti1-xAlxN coatings with different Al content were deposited on 1 Cr11Ni2W2MoV stainless steel for aero-engine compressor blades by arc ion plating. The results show that all coatings have a B1NaCl structure and the preferred orientation changes from (111) to (220) with increasing Al content; the lattice parameter of Ti1-xAlxN decreases with the increase of Al content. The oxidation-resistance of (Ti,Al)N coatings is significantly improved owing to the formation of Al-riched oxide on the surface of the coatings. The nitride coatings can significantly improve the corrosion-resistance of 1Cr11Ni2W2MoV stainless steel under the synergistic of water vapor and NaCl, and the corrosion-resistance becomes better when the Al content increases, because not only the quick formation of thin alumina layer prevents the further corrosion but also the formation of alumina seals the pinholes or defects in the coatings, which prevents the occurrence of localized nodules-like corrosion.
关键词	(Ti,Al)N arc ion plating oxidation-resistance corrosion-resistance
收录类别	SCI
语种	英语
WOS研究方向	Metallurgy & Metallurgical Engineering
WOS类目	Metallurgy & Metallurgical Engineering
WOS记录号	WOS:000241774000016
出版者	ALLERTON PRESS INC
引用统计
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/85570
专题	中国科学院金属研究所
通讯作者	Li Ming-sheng
作者单位	1.Jiangxi Sci & Technol Normal Univ, Jiangxi Key Lab Surface Engn, Nanchang 330013, Peoples R China 2.Chinese Acad Sci, Met Res Inst, State Lab Lab Corros & Protect, Shenyang 110016, Peoples R China
推荐引用方式 GB/T 7714	Li Ming-sheng,Feng Chang-jie,Zhang Zhi-feng,et al. Oxidation and corrosion behavior of titanium aluminum nitride coatings by arc ion plating[J]. TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA,2006,16:S75-S80.
APA	Li Ming-sheng,Feng Chang-jie,Zhang Zhi-feng,&Wang Fu-hui.(2006).Oxidation and corrosion behavior of titanium aluminum nitride coatings by arc ion plating.TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA,16,S75-S80.
MLA	Li Ming-sheng,et al."Oxidation and corrosion behavior of titanium aluminum nitride coatings by arc ion plating".TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA 16(2006):S75-S80.