Glass formation in the ternary Zr-Zr2Cu-Zr2Ni system

doi:10.1016/j.jnoncrysol.2006.01.083

IMR OpenIR

	Glass formation in the ternary Zr-Zr2Cu-Zr2Ni system
	Yang, H.; Wang, J. Q.; Li, Y.
通讯作者	Wang, J. Q.(jqwang@imr.ac.cn)
	2006-06-01
发表期刊	JOURNAL OF NON-CRYSTALLINE SOLIDS
ISSN	0022-3093
卷号	352 期号:8 页码:832-836
摘要	Glass formation and glass forming ability in the ternary Zr-Cu-Ni system were studied systematically. For Cu mold casting, the critical size for glass formation was found to be 1 mm in a relatively wide composition range of 56-64 at.% Zr, 16-26 at.% 3Cu and 16-24 at.% Ni. The phases competing with glass formation were found to be Zr, Zr2Cu and Zr2Ni. Despite the fact that Cu and Ni are completely miscible with each other, they cannot be regarded as simple substitution to each other in the case of glass formation in the Zr-Zr2Cu-Zr2Ni ternary eutectic system. (c) 2006 Published by Elsevier B.V.
关键词	amorphous metals metallic glasses transition metals glass formation thermal properties calorimetry glass transition X-ray diffraction
DOI	10.1016/j.jnoncrysol.2006.01.083
收录类别	SCI
语种	英语
WOS研究方向	Materials Science
WOS类目	Materials Science, Ceramics ; Materials Science, Multidisciplinary
WOS记录号	WOS:000237751000015
出版者	ELSEVIER SCIENCE BV
引用统计	被引频次：14[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/86747
专题	中国科学院金属研究所
通讯作者	Wang, J. Q.
作者单位	1.CAS, Met Res Inst, Shenyang Natl Lab Mat Sci, Shenyang 110016, Peoples R China 2.Natl Univ Singapore, Dept Mat Sci, Fac Sci, Singapore 117548, Singapore
推荐引用方式 GB/T 7714	Yang, H.,Wang, J. Q.,Li, Y.. Glass formation in the ternary Zr-Zr2Cu-Zr2Ni system[J]. JOURNAL OF NON-CRYSTALLINE SOLIDS,2006,352(8):832-836.
APA	Yang, H.,Wang, J. Q.,&Li, Y..(2006).Glass formation in the ternary Zr-Zr2Cu-Zr2Ni system.JOURNAL OF NON-CRYSTALLINE SOLIDS,352(8),832-836.
MLA	Yang, H.,et al."Glass formation in the ternary Zr-Zr2Cu-Zr2Ni system".JOURNAL OF NON-CRYSTALLINE SOLIDS 352.8(2006):832-836.