MgCl2对锌在干湿交替环境中腐蚀行为的影响
其他题名Effect of MgCl2 Deposite on Simulated Atmospheric Corrosion of Zn via Wet-dry Altertnating Corrosion Test
尹奇1; 刘淼然1; 刘雨薇1; 潘晨1; 王振尧1
2019
发表期刊材料研究学报
ISSN1005-3093
卷号000期号:009页码:705-712
摘要使用腐蚀失重、X射线衍射(XRD)、扫描电子显微镜与能谱(SEM-EDS)等手段研究了干湿交替环境中MgCl2对锌腐蚀行为的影响。结果表明,MgCl2对锌的腐蚀有显著的抑制作用;在沉积NaCl条件下锌表面的腐蚀产物为Zn5(OH)8Cl2·H2O、Zn4CO3(OH)6·H2O和Zn(OH)2,而在沉积MgCl2条件下锌表面的腐蚀产物只有Zn5(OH)8Cl2·H2O。在干湿交替环境中MgCl2对锌腐蚀行为的影响主要是Mg2+与氧还原反应产生的OH-结合使阴极区的pH值降低造成的。
其他摘要The effect of MgCl2-and NaCl-deposit on simulated atmospheric corrosion of Zn was comparatively investigated via wet-dry alternating corrosion test,as well as mass loss,X-ray diffraction(XRD),scanning electron microscope equipped with energy dispersive spectrometer(SEM-EDS).The results show that the corrosion rate of Zn was significantly inhibited by the deposition of MgCl2;the corrosion products formed on Zn plate with NaCl deposit were Zn5(OH)8 Cl2·H2 O、Zn4 CO3(OH)6·H2 O and Zn(OH)2,while was only Zn5(OH)8 Cl2·H2 O for Zn plate with MgCl2 deposit.It was proposed that the corrosion may be caused by the decrease of pH,which was induced by the precipitation of Mg2+ions and OH-ions,in the cathodic sites.
关键词材料失效与保护 大气腐蚀机制 室内模拟加速腐蚀实验 MgCl2 锌
收录类别CSCD
语种中文
CSCD记录号CSCD:6573012
引用统计
文献类型期刊论文
条目标识符http://ir.imr.ac.cn/handle/321006/87180
专题中国科学院金属研究所
作者单位1.中国科学院金属研究所
2.中国科学技术大学
3.中国科学院研究生院
推荐引用方式
GB/T 7714		 尹奇,刘淼然,刘雨薇,等. MgCl2对锌在干湿交替环境中腐蚀行为的影响[J]. 材料研究学报,2019,000(009):705-712.
APA 尹奇,刘淼然,刘雨薇,潘晨,&王振尧.(2019).MgCl2对锌在干湿交替环境中腐蚀行为的影响.材料研究学报,000(009),705-712.
MLA 尹奇,et al."MgCl2对锌在干湿交替环境中腐蚀行为的影响".材料研究学报 000.009(2019):705-712.
条目包含的文件
条目无相关文件。
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[尹奇]的文章
[刘淼然]的文章
[刘雨薇]的文章
百度学术
百度学术中相似的文章
[尹奇]的文章
[刘淼然]的文章
[刘雨薇]的文章
必应学术
必应学术中相似的文章
[尹奇]的文章
[刘淼然]的文章
[刘雨薇]的文章
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。