两步水热法制备BiOCl-RGO纳米复合材料及其光催化性能

IMR OpenIR

	两步水热法制备BiOCl-RGO纳米复合材料及其光催化性能
其他题名	Microstructures and Photocatalytic Properties of BiOCl-RGO Nanocomposites Prepared by Two-step Hydrothermal Method
	秦艳利 1; 杨艳 1; 赵鹏羽 1; 刘振宇 2; 倪丁瑞 2
	2020
发表期刊	材料研究学报
ISSN	1005-3093
卷号	000 期号:002 页码:92-100
摘要	用两步水热法合成了BiOCl-RGO复合材料。先在乙二醇和去离子水的混合溶液中合成直径约为400 nm、由纳米片构成的微球状单一BiOCl样品,在此基础上引入RGO载体制备出BiOCl-RGO纳米复合材料。使用Raman光谱、XRD、XPS等手段表征样品的物相构成,用SEM和TEM观测其微观形貌,通过降解甲基橙评定样品的光催化性能。结果表明,水热温度显著影响复合材料的光催化性能,在140℃制备的BiOCl和石墨烯结合的样品具有最高的光催化性能。
其他摘要	Composites of BiOCl-RGO were synthesized via a two-step hydrothermal method.Firstly plain BiOCl was synthesized in the mixed solution of ethylene glycol and deionized water,the acquired nanosphere-like BiOCl of about 400 nm in diameter composed of many nanosheets.Then the RGO carrier was deposited onto the plain BiOCl to prepare BiOCl-RGO nanocomposites.The composites were characterized by Raman spectroscopy,XRD,XPS,SEM and TEM.The photocatalytic property of the composites was evaluated by degrading methyl orange.The results show that the temperature of hydrothermal process significantly affects the photocatalytic property of the composites.The composite of BiOCl-graphene prepared at 140°C shows the highest photocatalytic performance.
关键词	复合材料氯氧化铋石墨烯水热法光催化性能
收录类别	CSCD
语种	中文
CSCD记录号	CSCD:6661971
引用统计	被引频次：4[CSCD] [CSCD记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/87485
专题	中国科学院金属研究所
作者单位	1.沈阳理工大学 2.中国科学院金属研究所
推荐引用方式 GB/T 7714	秦艳利,杨艳,赵鹏羽,等. 两步水热法制备BiOCl-RGO纳米复合材料及其光催化性能[J]. 材料研究学报,2020,000(002):92-100.
APA	秦艳利,杨艳,赵鹏羽,刘振宇,&倪丁瑞.(2020).两步水热法制备BiOCl-RGO纳米复合材料及其光催化性能.材料研究学报,000(002),92-100.
MLA	秦艳利,et al."两步水热法制备BiOCl-RGO纳米复合材料及其光催化性能".材料研究学报 000.002(2020):92-100.