Alternative TitleInvestigation of Anodic Film on a Novel RE-containing Al-Alloy Al-Zn-Mg-Cu-Sc
王英君1; 刘洪雷1; 王国军1; 董凯辉2; 宋影伟2; 倪丁瑞2
Source Publication中国腐蚀与防护学报
Abstract针对添加稀土Sc的新型高强7000系铝合金中析出相的特征,发展了相应的阳极氧化工艺,并通过封孔后处理进一步提高膜层的致密性。结果表明,在7000系稀土铝合金表面存在的含Sc析出相作为微阴极,加速其周围Al基体的溶解,影响成膜均匀性。通过调整氧化溶液组成及电参数,在铝合金表面获得了均匀的阳极氧化膜。同时对比了氟锆酸盐、铈盐及沸水3种封孔工艺对阳极氧化膜耐蚀性的影响,结果显示沸水封孔后的阳极氧化膜呈银白色,膜层均匀致密,无缺陷和微裂纹存在,耐蚀性最佳,该膜层盐雾测试336 h未发生腐蚀,可以满足实际工业应用的要求。
Other AbstractA novel anodic process was developed for a RE-containing 7000 series Al-alloy Al-Zn-Mg-Cu-Sc.Further,sealing-pore post treatments were carried out to improve the compactness of the anodic film.The results indicate that the precipitated Sc-containing phases on the surface of 7000 series Al-alloy act as micocathodes to accelerate the corrosion of Al matrix,which has a negative effect on the uniformity of the anodic film.In order to solve this trouble,the formula and electric parameters of the electrolyte bath were adjusted,hence,a uniform and smooth anodic film is formed on the surface of the Al-alloy.Meantime,three sealing-pore processes with fluozirconate,cerate and boiling water respectively were carried out to improve the compactness of the anodic film.It is found that after boiling water sealing-pore,the anodic film exhibits a sliver like uniform surface without defects and microcracks,among others,that film presents the best corrosion resistance,and the film can keep intact after salt spray test for 336 h,which can satisfy the requirement for the actual applications.
Keyword稀土铝合金 析出相 阳极氧化 封孔处理 耐蚀性
Indexed ByCSCD
Citation statistics
Cited Times:6[CSCD]   [CSCD Record]
Document Type期刊论文
Recommended Citation
GB/T 7714
王英君,刘洪雷,王国军,等. 新型高强稀土Al-Zn-Mg-Cu-Sc铝合金的阳极氧化及其抗腐蚀性能研究[J]. 中国腐蚀与防护学报,2020,40.0(002):131-138.
APA 王英君,刘洪雷,王国军,董凯辉,宋影伟,&倪丁瑞.(2020).新型高强稀土Al-Zn-Mg-Cu-Sc铝合金的阳极氧化及其抗腐蚀性能研究.中国腐蚀与防护学报,40.0(002),131-138.
MLA 王英君,et al."新型高强稀土Al-Zn-Mg-Cu-Sc铝合金的阳极氧化及其抗腐蚀性能研究".中国腐蚀与防护学报 40.0.002(2020):131-138.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[王英君]'s Articles
[刘洪雷]'s Articles
[王国军]'s Articles
Baidu academic
Similar articles in Baidu academic
[王英君]'s Articles
[刘洪雷]'s Articles
[王国军]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[王英君]'s Articles
[刘洪雷]'s Articles
[王国军]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.