Initial corrosion behavior of carbon steel Q235 in the atmosphere with SO2 | |
Wang Chuan; Wang Zhenyao; Ke Wei | |
通讯作者 | Wang Zhenyao(zhywang@imr.ac.cn) |
2008-06-01 | |
发表期刊 | ACTA METALLURGICA SINICA
![]() |
ISSN | 0412-1961 |
卷号 | 44期号:6页码:729-734 |
摘要 | The initial corrosion behaviors of carbon steel Q235 in the atmosphere with different concentrations Of SO2 were investigated by SEM/EDAX and FTIR. The corrosion kinetics results showed the variation of thickness loss of Q235 is related to concentrations Of SO2. When the concentration Of SO2 was relatively low, the thickness loss increased slowly, and when the concentration Of SO2 was relatively high, the thickness loss decreased rapidly. The concentration Of SO2 has a little effect on sulfate in the products, but facilitated the formations of oxide or hydrate in the rust layer. In all conditions, the corrosion products included FeSO4 center dot 7H(2)O, Fe-2(SO4)(3)center dot 9H(2)O, gamma-FeOOH and amorphous delta-FeOOH, but the concentration Of SO2 was enhanced to 0.5% (volume fraction), alpha-FeOOH was detected in the corrosion products. In the atmosphere with 0.05%SO2, rust nests appeared in the rust layer and the elements inside and outside the nest were great different, and a probable mechanism was proposed. |
关键词 | steel Q235 SO2 initial corrosion rust nest |
收录类别 | SCI |
语种 | 英语 |
WOS研究方向 | Metallurgy & Metallurgical Engineering |
WOS类目 | Metallurgy & Metallurgical Engineering |
WOS记录号 | WOS:000257410200017 |
出版者 | SCIENCE CHINA PRESS |
引用统计 | |
文献类型 | 期刊论文 |
条目标识符 | http://ir.imr.ac.cn/handle/321006/93219 |
专题 | 中国科学院金属研究所 |
通讯作者 | Wang Zhenyao |
作者单位 | Chinese Acad Sci, Inst Met Res, Environm Corros Ctr, Shenyang 110016, Peoples R China |
推荐引用方式 GB/T 7714 | Wang Chuan,Wang Zhenyao,Ke Wei. Initial corrosion behavior of carbon steel Q235 in the atmosphere with SO2[J]. ACTA METALLURGICA SINICA,2008,44(6):729-734. |
APA | Wang Chuan,Wang Zhenyao,&Ke Wei.(2008).Initial corrosion behavior of carbon steel Q235 in the atmosphere with SO2.ACTA METALLURGICA SINICA,44(6),729-734. |
MLA | Wang Chuan,et al."Initial corrosion behavior of carbon steel Q235 in the atmosphere with SO2".ACTA METALLURGICA SINICA 44.6(2008):729-734. |
条目包含的文件 | 条目无相关文件。 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论