Preparation of TiAl3-Al composite coating by cold spraying

doi:10.1016/S1003-6326(08)60369-6

IMR OpenIR

	Preparation of TiAl3-Al composite coating by cold spraying
	Shen Li; Kong Ling-yan; Xiong Tian-ying; Du Hao; Li Tie-fan
通讯作者	Xiong Tian-ying(tyxiong@imr.ac.cn)
	2009-08-01
发表期刊	TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA
ISSN	1003-6326
卷号	19 期号:4 页码:879-882
摘要	TiAl3-Al coating was deposited on orthorhombic Ti2AlNb alloy substrate by cold spraying with the mixture of pure Al and Ti as the feedstock powder at a fixed molar ratio of 3:1 when the spraying distance, gas temperature and gas pressure for the process were 10 mm, 250 degrees C and 1.8 MPa, respectively. The as-sprayed coating was then subjected to heat treatment at 630 degrees C in argon atmosphere for 5 h at a heating rate of 3 degrees C/min and an argon gas flow rate of 40 mL/min. The obtained TiAl3-Al composite coating is about 212 mu m with a density of 3.16 g/cm(3) and a porosity of 14.69% in general. The microhardness and bonding strength for the composite coating are HV525 and 27.12 MPa.
关键词	cold spraying TiAl3-Al composite coating orthorhombic Ti2AlNb alloy high temperature oxidation
DOI	10.1016/S1003-6326(08)60369-6
收录类别	SCI
语种	英语
WOS研究方向	Metallurgy & Metallurgical Engineering
WOS类目	Metallurgy & Metallurgical Engineering
WOS记录号	WOS:000269099300020
出版者	ELSEVIER SCIENCE BV
引用统计	被引频次：30[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.imr.ac.cn/handle/321006/97588
专题	中国科学院金属研究所
通讯作者	Xiong Tian-ying
作者单位	Chinese Acad Sci, State Key Lab Corros & Protect, Inst Met Res, Shenyang 110016, Peoples R China
推荐引用方式 GB/T 7714	Shen Li,Kong Ling-yan,Xiong Tian-ying,et al. Preparation of TiAl3-Al composite coating by cold spraying[J]. TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA,2009,19(4):879-882.
APA	Shen Li,Kong Ling-yan,Xiong Tian-ying,Du Hao,&Li Tie-fan.(2009).Preparation of TiAl3-Al composite coating by cold spraying.TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA,19(4),879-882.
MLA	Shen Li,et al."Preparation of TiAl3-Al composite coating by cold spraying".TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA 19.4(2009):879-882.