Estimation of the size of GBF area on fracture surface for high strength steels in very high cycle fatigue regime 期刊论文
International Journal of Fatigue, 2008, 卷号: 30, 期号: 6, 页码: 1016-1023
作者:  Z. G. Yang;  S. X. Li;  Y. B. Liu;  Y. D. Li;  G. Y. Li;  W. J. Hui;  Y. Q. Weng
Adobe PDF(830Kb)  |  收藏  |  浏览/下载：114/0  |  提交时间：2012/04/13
High Strength Steel  Very High Cycle Fatigue  Granular Bright Facet  (Gbf)  Hydrogen  The Maximum Size Of The Plastic Zone  Fatigue Crack  Growth Rate  Subsurface Crack Initiation  Chromium-bearing Steel  Long-life Fatigue  N-greater-than-10(7) Cycles  Part Ii  Mechanism  Failure  Hydrogen  Inclusions  Behavior